Description

FLEX NORYL™ WCD891B resin is a flexible, non-reinforced extrudable blend of Polyphenylene Ether (PPE) + Thermoplastic Elastomer (TPE). This material contains non-halogenated flame retardant and performance capable of meeting UL VW-1 requirements, 80C end use temperature rating, and heat deformation performance as defined by UL 1581. FLEX NORYL WCD891B resin is intended for evaluation in wire and cable applications in dark colors. It has a Shore A Hardness reading of 89 and exhibits superior thermal stability, very low water absorption, good electric properties, and low specific gravity. Processing is typically conducted on standard extrusion equipment, and UL 1581 testing is conducted on 2.0mm wire with 0.12mm X 20 stranded copper conductor.

Diese Materialdaten wurden von Sabic zur Verfügung gestellt

Alle Daten beziehen sich auf Raumtemperatur soweit nicht anderweitig spezifiziert. SI Einheiten werden verwendt soweit nicht anderweitig spezifiziert.
Äquivalente Standards sind ähnlich zu einem oder mehreren Standards die der Anbieter angegeben hat. Manche äquivalente Standards können strikter sein oder außerhalb der Bedingungen des ursprünglichen Standards.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Anwendungen

Herstellung

Oberflächenbearbeitung und -beschichtung

Metallbeschichtungen

Elektrotechnik

Elektronik

Anzeigegeräte

Konsumgüter

General Appliances

Materialien von diesem Anbieter

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

Sehen Sie alle Materialen dieses Anbieters

Eigenschaften

Allgemein

Property	Temperature	Value	Comment
Relative Dichte	23.0 °C	1.1 [-] Show Supplier Material materials with Relative Dichte of 1.1 [-]	ASTM D 792 \|
Sauerstoffindex	23.0 °C	27 % Show Supplier Material materials with Sauerstoffindex of 27 %

Mechanisch

Property	Temperature	Value	Comment
Biegemodul	23.0 °C	0.1 GPa Show Supplier Material materials with Biegemodul of 0.1 GPa	ISO 178 \| 12.5 mm/min
Dehnung	23.0 °C	140 % Show Supplier Material materials with Dehnung of 140 %	ISO 527 \| yield, 50 mm/min
Härte, Shore A	23.0 °C	89 [-] Show Supplier Material materials with Härte, Shore A of 89 [-]	ASTM D 2240 \| 30S reading
Zugfestigkeit	23.0 °C	15 MPa Show Supplier Material materials with Zugfestigkeit of 15 MPa	ISO 527 \| break, 50 mm/min

Thermisch

Property	Value	Comment
Brittleness temperature	-40 °C Show Supplier Material materials with Brittleness temperature of -40 °C	<, ASTM D 746

Elektrisch

Property	Temperature	Value	Comment
Dielektrizitätskonstante, 1 MHz	23.0 °C	2.9 [-] Show Supplier Material materials with Dielektrizitätskonstante, 1 MHz of 2.9 [-]	IEC 60250
Dissipation factor, 1MHz	23.0 °C	0.04 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 0.04 [-]	IEC 60250
Durchschlagfestigkeit	23.0 °C	24 kV/mm Show Supplier Material materials with Durchschlagfestigkeit of 24 kV/mm	IEC 60243-1 \| in oil, 2.0mm
Kriechstromfestigkeit	23.0 °C	600 V Show Supplier Material materials with Kriechstromfestigkeit of 600 V	IEC 60112 \|
Sheet resistivity, ROA	23.0 °C	5.10E+15 Ω Show Supplier Material materials with Sheet resistivity, ROA of 5.10E+15 Ω	ASTM D 257
Volume resistivity	23.0 °C	1.50E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 1.50E+15 Ω·cm	ASTM D 257

Rheological Properties

Property	Value	Comment
Schmelzmassenflussrate	20 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 20 g/10min	ASTM D 1238 \| 250°C/5.0 kgf

Technological properties

Property
Application areas	ATM/Ticket Machine, Enclosure/Housing/Cover, Wire Coatings, Wireless Communications, Wire & cable
Availability	Europe,Asia,Americas
Processing methods	Conductor Pre-heat Temperature: 25 to 120.0°C Melt Temperature: 220 to 250.0°C Screw Speed: 15 to 85.0rpm Drying Time: 5 to 7.0hrs Maximum Moisture Content: 0.02% Neck Temperature: 220 to 250.0°C Head Zone Temperature: 220 to 250.0°C Water Bath Temperature: 15 to 60.0°C Cross-head Temperature: 220 to 250.0°C Cooling Water Air Gap: 100 to 200.0mm Die Temperature: 220 to 250.0°C Feed Zone Temperature: 180 to 220.0°C Drying Temperature: 75 to 85.0°C Middle Zone Temperatures: 220 to 250.0°C Drying Time (Cumulative): 12hrs Screen Pack: 150 to 100.0- Extruder Length/Diameter Ratio (L/D): 22:1 to 26:1-
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.