Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.24 g/cm³ Show Supplier Material materials with Dichte of 1.24 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.06 % Show Supplier Material materials with Moisture absorption of 0.06 % | ISO 62 | (23°C / 50% RH) |
Relative Dichte | 23.0 °C | 1.24 [-] Show Supplier Material materials with Relative Dichte of 1.24 [-] | ASTM D 792 | |
Sauerstoffindex | 23.0 °C | 23 % Show Supplier Material materials with Sauerstoffindex of 23 % | |
Wasserabsorption | 23.0 °C | 0.15 % Show Supplier Material materials with Wasserabsorption of 0.15 % | ISO 62-1 | (23°C/saturated) |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 135 MPa Show Supplier Material materials with Biegefestigkeit of 135 MPa | ISO 178 | break, 2 mm/min |
Biegemodul | 23.0 °C | 4.5 GPa Show Supplier Material materials with Biegemodul of 4.5 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 2 % Show Supplier Material materials with Dehnung of 2 % | ISO 527 | break, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 6 GPa Show Supplier Material materials with Elastizitätsmodul of 6 GPa | ISO 527 | 1 mm/min |
Hardness, Ball Indentation | 23.0 °C | 100 MPa Show Supplier Material materials with Hardness, Ball Indentation of 100 MPa | ISO 2039-1 | H358/30 |
Impact strength, Izod notched, ASTM | 23.0 °C | 60 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 60 J/m | ASTM D 256 |
Instrumented Impact, Total Energy | 23.0 °C | 14 J Show Supplier Material materials with Instrumented Impact, Total Energy of 14 J | ASTM D 3763 | 23°C |
Schlagzähigkeit, Charpy ungekerbt | 23.0 °C | 25 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 25 kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*4 sp=62mm, -30°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 60 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 60 kJ/m² | ASTM D 256 | notched, 23°C |
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 25 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod ungekerbt of 25 kJ/m² | ISO 180/1U | 80*10*4, 23°C |
Taber Abrasion | 23.0 °C | 45 mg/1000cy Show Supplier Material materials with Taber Abrasion of 45 mg/1000cy | SABIC method | CS-17, 1 kg |
Zugfestigkeit | 23.0 °C | 90 MPa Show Supplier Material materials with Zugfestigkeit of 90 MPa | ISO 527 | break, 5 mm/min |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Ball Pressure Test | nan | IEC 60695-10-2 | 125°C +/- 2°C | |||
Ball pressure temperature | 165 °C Show Supplier Material materials with Ball pressure temperature of 165 °C | IEC 60695-10-2 | approximate maximum | |||
Heat deflection temperature, 0.45 MPa | 170 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 170 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm | |||
Heat deflection temperature, 1.80 MPa | 160 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 160 °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 3E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 3E-5 1/K | ISO 11359-2 | 23°C to 80°C | ||
Vicat-Erweichungstemperatur | 180 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 180 °C | ISO 306 | Rate B/120 | |||
Wärmeformbeständigkeitstemperatur | 160 - 170 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 160 - 170 °C | ||||
Wärmeleitfähigkeit | 23.0 °C | 0.26 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 0.26 W/(m·K) | ISO 8302 | ||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 7E-5 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 7E-5 1/K | ISO 11359-2 | 23°C to 80°C | ||
Entflammbarkeit | UL Recognized, 94HB Flame Class Rating: ≥1.5mm UL 94 <br> Glow Wire Flammability Index 960°C, passes at: 3.2mm IEC 60695-2-12 <br> Glow Wire Flammability Index 960°C, passes at: 3.2mm IEC 60695-2-12 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=236755- - | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielectric constant, 60Hz | 23.0 °C | 2.7 [-] Show Supplier Material materials with Dielectric constant, 60Hz of 2.7 [-] | IEC 60250 | 50/60 Hz |
Dielektrizitätskonstante, 1 MHz | 23.0 °C | 2.6 [-] Show Supplier Material materials with Dielektrizitätskonstante, 1 MHz of 2.6 [-] | IEC 60250 |
Dissipation factor, 1MHz | 23.0 °C | 2E-3 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 2E-3 [-] | IEC 60250 |
Dissipation factor, 50Hz | 23.0 °C | 6E-3 [-] Show Supplier Material materials with Dissipation factor, 50Hz of 6E-3 [-] | IEC 60250 | 50/60 Hz |
Durchschlagfestigkeit | 23.0 °C | 16 kV/mm Show Supplier Material materials with Durchschlagfestigkeit of 16 kV/mm | IEC 60243-1 | in oil, 3.2 mm, |
Kriechstromfestigkeit | 23.0 °C | 200 V Show Supplier Material materials with Kriechstromfestigkeit of 200 V | IEC 60112 | |
Sheet resistivity, ROA | 23.0 °C | 1.00E+15 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1.00E+15 Ω | >, IEC 60093 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+15 Ω·cm | IEC 60093 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 4.5 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 4.5 g/10min | ASTM D 1238 | 300°C/5.0 kgf | |
Schmelzvolumenflussrate | 11 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 11 cm³/10min | ISO 1133 | MVR at 300°C/10.0 kg | |
Schrumpfung | 23.0 °C | 0.2 % Show Supplier Material materials with Schrumpfung of 0.2 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Freezer, Electrical, EV/HEV Battery, Industrial Material Handling, Heavy Vehicles, Hot Water System, Electronic Components, Enclosures, Auto Aftermarket, Cooking Range, Washing Machine, Underhood, Wiring Devices, Wireless Communications, Pump, Ignition System, Microwave Oven, Motorcycle, Personal Computing | |
| Availability | Europe | |
| Processing methods | Mold Temperature: 80 to 120.0°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |