Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.11 g/cm³ Show Supplier Material materials with Dichte of 1.11 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.05 % Show Supplier Material materials with Moisture absorption of 0.05 % | ISO 62 | (23°C / 50% RH) |
Relative Dichte | 23.0 °C | 1.11 [-] Show Supplier Material materials with Relative Dichte of 1.11 [-] | ASTM D 792 | |
Sauerstoffindex | 23.0 °C | 33 % Show Supplier Material materials with Sauerstoffindex of 33 % | |
Wasserabsorption | 23.0 °C | 0.2 % Show Supplier Material materials with Wasserabsorption of 0.2 % | ISO 62-1 | (23°C/saturated) |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 100 MPa Show Supplier Material materials with Biegefestigkeit of 100 MPa | ISO 178 | yield, 2 mm/min |
Biegemodul | 23.0 °C | 2.4 GPa Show Supplier Material materials with Biegemodul of 2.4 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 8.3 % Show Supplier Material materials with Dehnung of 8.3 % | ISO 527 | break, 50 mm/min |
Elastizitätsmodul | 23.0 °C | 2.4 GPa Show Supplier Material materials with Elastizitätsmodul of 2.4 GPa | ISO 527 | 1 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 300 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 300 J/m | ASTM D 256 |
Instrumented Impact, Total Energy | 23.0 °C | 52 J Show Supplier Material materials with Instrumented Impact, Total Energy of 52 J | ASTM D 3763 | 23°C |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 20 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 20 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, 23°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 14 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 14 kJ/m² | ISO 180/1A | 80*10*4, -30°C |
Zugfestigkeit | 23.0 °C | 58 MPa Show Supplier Material materials with Zugfestigkeit of 58 MPa | ISO 527 | break, 50 mm/min |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 124 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 124 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 6.7E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 6.7E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Vicat-Erweichungstemperatur | 143 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 143 °C | ISO 306 | Rate B/50 | |||
Wärmeformbeständigkeitstemperatur | 124 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 124 °C | ||||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 6.7E-5 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 6.7E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Entflammbarkeit | Ds_4min: 70- ISO 5659-2 <br> Lateral Flame Spread, CFE: 20kW/m² ISO 5658-2 <br> M1 Flame Class Rating: 2mm NF P 92501 <br> Glow Wire Ignitability Temperature, 1.0 mm: 775°C IEC 60695-2-13 <br> Flame Spread Index (1.52mm): 15- ASTM E 162 <br> NBS Smoke Density, Non-Flaming, 4 min (1.52mm): 7- ASTM E 662 <br> Toxicity (3 mm): 21.76- NF X70-100 <br> NBS Smoke Density, Flaming, 4 min (1.52mm): 30- ASTM E 662 <br> NBS Smoke Density, Flaming, 4 min (3.2 mm): 30- ASTM E 662 <br> Heat Release, MAHRE: 33.6kW/m² ISO 5660-1 <br> Toxicity: 0- ISO 5659-2 <br> F1 Class Smoke and Toxicity Rating: 3mm NF F16-101 <br> NBS Smoke Density, Flaming, 20 min (3.2 mm): 120- ASTM E 662 <br> Glow Wire Flammability Index, 1.0 mm: 960°C IEC 60695-2-12 <br> Glow Wire Flammability Index, 1.5 mm: 960°C IEC 60695-2-12 <br> Glow Wire Ignitability Temperature, 1.5 mm: 775°C IEC 60695-2-13 <br> UL Recognized, 94V-0 Flame Class Rating: ≥1.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=100050086- - |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dielektrizitätskonstante, 1 MHz | 23.0 °C | 2.7 [-] Show Supplier Material materials with Dielektrizitätskonstante, 1 MHz of 2.7 [-] | IEC 60250 |
Dissipation factor, 1MHz | 23.0 °C | 2.9E-3 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 2.9E-3 [-] | IEC 60250 |
Durchschlagfestigkeit | 23.0 °C | 34.1 kV/mm Show Supplier Material materials with Durchschlagfestigkeit of 34.1 kV/mm | IEC 60243-1 | in oil, 3.2 mm, |
Sheet resistivity, ROA | 23.0 °C | 1.25E+18 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1.25E+18 Ω | IEC 60093 |
Volume resistivity | 23.0 °C | 7.62E+17 Ω·cm Show Supplier Material materials with Volume resistivity of 7.62E+17 Ω·cm | IEC 60093 | |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzmassenflussrate | 5.6 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 5.6 g/10min | ASTM D 1238 | 280°C/5.0 kgf | |
Schmelzvolumenflussrate | 5 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 5 cm³/10min | ISO 1133 | MVR at 280°C/5.0 kg | |
Schrumpfung | 23.0 °C | 0.5 % Show Supplier Material materials with Schrumpfung of 0.5 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Exterior Rail Components, Fuel Cell, Rail, Wiring Devices, Wire & cable | |
Availability | Europe,Asia,Americas | |
Processing methods | Barrel - Zone 1 Temperature: 220 to 260.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |