Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.19 g/cm³ Show Supplier Material materials with Dichte of 1.19 g/cm³ | ISO 1183 |
Relative Dichte | 23.0 °C | 1.19 [-] Show Supplier Material materials with Relative Dichte of 1.19 [-] | ASTM D 792 |
Sauerstoffindex | 23.0 °C | 48 % Show Supplier Material materials with Sauerstoffindex of 48 % | |
Wasserabsorption | 23.0 °C | 0.58 % Show Supplier Material materials with Wasserabsorption of 0.58 % | ISO 62-1 | (23°C/24hrs) |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 55 MPa Show Supplier Material materials with Biegefestigkeit of 55 MPa | ISO 178 | yield, 2 mm/min |
Biegemodul | 23.0 °C | 1.3 GPa Show Supplier Material materials with Biegemodul of 1.3 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 74 % Show Supplier Material materials with Dehnung of 74 % | ISO 527 | break, 50 mm/min |
Elastizitätsmodul | 23.0 °C | 1.4 GPa Show Supplier Material materials with Elastizitätsmodul of 1.4 GPa | ISO 527 | 1 mm/min |
Härte, Shore D | 23.0 °C | 72 [-] Show Supplier Material materials with Härte, Shore D of 72 [-] | ASTM D 2240 |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 25 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 25 kJ/m² | ISO 180/1A | 80*10*4, -30°C |
Taber Abrasion | 23.0 °C | 50 mg/1000cy Show Supplier Material materials with Taber Abrasion of 50 mg/1000cy | ASTM D 1044 | CS-17, 1 kg |
Zugfestigkeit | 23.0 °C | 41 MPa Show Supplier Material materials with Zugfestigkeit of 41 MPa | ISO 527 | break, 50 mm/min |
Thermisch
Property | Value | Comment | |
---|---|---|---|
Glasübergangstemperatur | 195 °C Show Supplier Material materials with Glasübergangstemperatur of 195 °C | DMA | matrix | |
Heat deflection temperature, 0.45 MPa | 144 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 144 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |
Vicat-Erweichungstemperatur | 167 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 167 °C | ISO 306 | Rate B/120 | |
Wärmeformbeständigkeitstemperatur | 144 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 144 °C | ||
Entflammbarkeit | UL Compliant, 94V-0 Flame Class Rating: 1.6mm UL 94 by SABIC-IP |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric constant, 1KHz | 23.0 °C | 3 [-] Show Supplier Material materials with Dielectric constant, 1KHz of 3 [-] | ASTM D 150 |
Dielektrizitätskonstante, 1 MHz | 23.0 °C | 3.02 [-] Show Supplier Material materials with Dielektrizitätskonstante, 1 MHz of 3.02 [-] | ASTM D 150 |
Dielektrizitätskonstante, 100 Hz | 23.0 °C | 3.14 [-] Show Supplier Material materials with Dielektrizitätskonstante, 100 Hz of 3.14 [-] | ASTM D 150 |
Dissipation factor, 100Hz | 23.0 °C | 0.01 [-] Show Supplier Material materials with Dissipation factor, 100Hz of 0.01 [-] | ASTM D 150 |
Dissipation factor, 100kHz | 23.0 °C | 6.4E-3 [-] Show Supplier Material materials with Dissipation factor, 100kHz of 6.4E-3 [-] | ASTM D 150 |
Dissipation factor, 1MHz | 23.0 °C | 5.5E-3 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 5.5E-3 [-] | ASTM D 150 | |
Durchschlagfestigkeit | 23.0 °C | 16.6 kV/mm Show Supplier Material materials with Durchschlagfestigkeit of 16.6 kV/mm | ASTM D 149 | in oil, 3.2 mm |
Sheet resistivity, ROA | 23.0 °C | 1.00E+15 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1.00E+15 Ω | >, ASTM D 257 |
Volume resistivity | 23.0 °C | 1.00E+16 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+16 Ω·cm | >, ASTM D 257 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzmassenflussrate | 8.6 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 8.6 g/10min | ASTM D 1238 | 295°C/6.6 kgf | |
Schrumpfung | 23.0 °C | 0.86 % Show Supplier Material materials with Schrumpfung of 0.86 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Fluid Delivery, Enclosure/Housing/Cover, Aerospace, Wire & cable | |
Availability | Europe,Americas | |
Processing methods | Drying Time (Cumulative): 8hrs | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |