NORYL™ Resin LS6010 - Europe

Want to keep this datasheet? Save it now in your required format

Description

NORYL™ LS6010 resin is a non-reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This high performance, injection moldable and extrudable grade contains non-brominated, non-chlorinated flame retardant and carries a UL94 flame rating of V0 at 1.5mm. NORYL LS6010 resin features low smoke production upon burning, high heat resistance, very low specific gravity, enhanced resistance to melting and dripping and meets the requirements of FAR 25.853. In addition, this material is heat stabilized and impact modified. It is an excellent candidate for aerospace interior applications such as rub strips, seat track covers, cable guides, switch panels, conduit, wall/ceiling mounted electronics, and parts machined from slab stock.

Diese Materialdaten wurden von Sabic zur Verfügung gestellt

Alle Daten beziehen sich auf Raumtemperatur soweit nicht anderweitig spezifiziert. SI Einheiten werden verwendt soweit nicht anderweitig spezifiziert.
Äquivalente Standards sind ähnlich zu einem oder mehreren Standards die der Anbieter angegeben hat. Manche äquivalente Standards können strikter sein oder außerhalb der Bedingungen des ursprünglichen Standards.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Anwendungen

Eisenbahn

Luft- und Raumfahrt

Materialien von diesem Anbieter

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

Sehen Sie alle Materialen dieses Anbieters

Eigenschaften

Allgemein

Property	Temperature	Value	Comment
Dichte	23.0 °C	1.11 g/cm³ Show Supplier Material materials with Dichte of 1.11 g/cm³	ISO 1183
Moisture absorption	23.0 °C	0.05 % Show Supplier Material materials with Moisture absorption of 0.05 %	ISO 62 \| (23°C / 50% RH)
Relative Dichte	23.0 °C	1.11 [-] Show Supplier Material materials with Relative Dichte of 1.11 [-]	ASTM D 792 \|
Wasserabsorption	23.0 °C	0.2 % Show Supplier Material materials with Wasserabsorption of 0.2 %	ISO 62-1 \| (23°C/saturated)

Mechanisch

Property	Temperature	Value	Comment
Biegefestigkeit	23.0 °C	100 MPa Show Supplier Material materials with Biegefestigkeit of 100 MPa	ISO 178 \| yield, 2 mm/min
Biegemodul	23.0 °C	2.4 GPa Show Supplier Material materials with Biegemodul of 2.4 GPa	ISO 178 \| 2 mm/min
Dehnung	23.0 °C	4.7 % Show Supplier Material materials with Dehnung of 4.7 %	ISO 527 \| yield, 50 mm/min
Elastizitätsmodul	23.0 °C	2.4 GPa Show Supplier Material materials with Elastizitätsmodul of 2.4 GPa	ISO 527 \| 1 mm/min
Impact strength, Izod notched, ASTM	23.0 °C	181 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 181 J/m	ASTM D 256
Instrumented Impact, Total Energy	23.0 °C	52 J Show Supplier Material materials with Instrumented Impact, Total Energy of 52 J	ASTM D 3763 \| 23°C
Schlagfestigkeit, Charpy gekerbt	23.0 °C	20 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 20 kJ/m²	ISO 179/1eA \| V-notch Edgew, 23°C, 80104 sp=62mm
Schlagzähigkeit, Izod gekerbt	23.0 °C	14 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 14 kJ/m²	ISO 180/1A \| 80104, -30°C
Zugfestigkeit	23.0 °C	58 MPa Show Supplier Material materials with Zugfestigkeit of 58 MPa	ISO 527 \| break, 50 mm/min

Thermisch

Property	Temperature	Value	Comment
Heat deflection temperature, 1.80 MPa		124 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 124 °C	ISO 75/Af \| Flatw 80104 sp=64mm
Koeffizient der thermischen Ausdehnung	23.0 °C	6.7E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 6.7E-5 1/K	ISO 11359-2 \| -40°C to 40°C
Vicat-Erweichungstemperatur		143 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 143 °C	ISO 306 \| Rate B/50
Wärmeformbeständigkeitstemperatur		124 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 124 °C
thermischer Ausdehnungskoeffizient, transversal	23.0 °C	6.7E-5 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 6.7E-5 1/K	ISO 11359-2 \| -40°C to 40°C
Entflammbarkeit	Vertical Burn b (12s, 1.52mm) passes at: 4sec FAR 25.853 <br> Vertical Burn a (60s, 1.52mm) passes at: 0sec FAR 25.853 <br> Flame Spread Index (1.52mm): 15- ASTM E 162 <br> NBS Smoke Density, Non-Flaming, 4 min (1.52mm): 7- ASTM E 662 <br> NBS Smoke Density, Flaming, 4 min (1.52mm): 30- ASTM E 662 <br> Draeger Tube Toxicity, Flaming (1.52mm): Pass- Based on ASTM E 662 <br> Draeger Tube Toxicity, Non-Flaming (1.52mm): Pass- Based on ASTM E 662

Rheological Properties

Property	Temperature	Value	Comment
Schmelzmassenflussrate		5.6 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 5.6 g/10min	ASTM D 1238 \| 280°C/5.0 kgf
Schmelzvolumenflussrate		5 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 5 cm³/10min	ISO 1133 \| MVR at 280°C/5.0 kg
Schrumpfung	23.0 °C	0.5 % Show Supplier Material materials with Schrumpfung of 0.5 %	SABIC method \| 3.2 mm

Technological properties

Property
Application areas	Air Cabin Interiors, Aerospace, Aircraft Seating, Interior Rail Components
Availability	Europe,Asia,Americas
Processing methods	Shot to Cylinder Size: 30 to 70.0% Maximum Moisture Content: 0.07% Barrel - Zone 2 Temperature: 220 to 260.0°C Drying Time (Cumulative): 12hrs Mold Temperature: 65 to 100.0°C Drying Time: 2 to 4.0hrs Roll Stack Temp - Middle: 90 to 150.0°C Middle - Zone 2 Temperature: 290 to 300.0°C Die Temperature: 220 to 260.0°C Drying Temperature: 95 to 105.0°C Nozzle Temperature: 295 to 305.0°C Front - Zone 3 Temperature: 295 to 305.0°C Adapter Temperature: 220 to 260.0°C Roll Stack Temp - Bottom: 90 to 150.0°C Roll Stack Temp - Top: 90 to 150.0°C Drying Time (Cumulative): 12hrs Barrel - Zone 3 Temperature: 220 to 260.0°C Drying Time (Cumulative): 12hrs Barrel - Zone 3 Temperature: 220 to 260.0°C Barrel - Zone 2 Temperature: 220 to 260.0°C Barrel - Zone 1 Temperature: 220 to 260.0°C Calibrator Temperature: 30 to 60.0°C Drying Temperature: 95 to 105.0°C Drying Temperature: 95 to 105.0°C Melt Temperature: 220 to 260.0°C Hopper Temperature: 80 to 120.0°C Melt Temperature: 280 to 305.0°C Die Temperature: 220 to 260.0°C Adapter Temperature: 220 to 260.0°C Barrel - Zone 4 Temperature: 220 to 260.0°C Rear - Zone 1 Temperature: 280 to 295.0°C Screw Speed: 40 to 80.0rpm Barrel - Zone 1 Temperature: 220 to 260.0°C Maximum Moisture Content: 0.07% Melt Temperature: 220 to 260.0°C Drying Time: 2 to 4.0hrs Barrel - Zone 4 Temperature: 220 to 260.0°C Drying Time: 2 to 4.0hrs Water Bath Temperature: 30 to 50.0°C
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.