Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Relative Dichte | 23.0 °C | 1.36 [-] Show Supplier Material materials with Relative Dichte of 1.36 [-] | ASTM D 792 | |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 193 MPa Show Supplier Material materials with Biegefestigkeit of 193 MPa | ASTM D 790 | yld, 2.6 mm/min, 100 mm span |
Biegemodul | 23.0 °C | 4.9 GPa Show Supplier Material materials with Biegemodul of 4.9 GPa | ASTM D 790 | 2.6 mm/min, 100 mm span |
Dehnung | 23.0 °C | 4 % Show Supplier Material materials with Dehnung of 4 % | ASTM D 638 | brk, Type I, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 4.8 GPa Show Supplier Material materials with Elastizitätsmodul of 4.8 GPa | ASTM D 638 | 5 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 37 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 37 J/m | ASTM D 256 |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 37 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 37 kJ/m² | ASTM D 256 | notched, 23°C |
Zugfestigkeit | 23.0 °C | 117 MPa Show Supplier Material materials with Zugfestigkeit of 117 MPa | ASTM D 638 | yld, Type I, 5 mm/min |
Thermisch
| Property | Value | Comment | |
|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 215 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 215 °C | ASTM D 648 | 6.4 mm, unannealed | |
Relative temperature index, electrical | 105 °C Show Supplier Material materials with Relative temperature index, electrical of 105 °C | UL 746B | |
Relative temperature index, mechanical impact | 105 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 105 °C | UL 746B | |
Relative temperature index, mechanical strength | 105 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 105 °C | UL 746B | |
Wärmeformbeständigkeitstemperatur | 215 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 215 °C | ||
Entflammbarkeit | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=221117- - <br> UL Recognized, 94-5VA Flame Class Rating: ≥1.5mm UL 94 <br> UL Recognized, 94V-0 Flame Class Rating: ≥1.5mm UL 94 | ||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
High Amp Arc Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm | ≥, UL 746A | PLC 3 |
High Volt Arc Track Rate | 23.0 °C | 3 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 3 PLC Code | UL 746A | (PLC) |
Hot-Wire Ignition | 23.0 °C | 3 mm Show Supplier Material materials with Hot-Wire Ignition of 3 mm | ≥, UL 746A | PLC 0 |
Kriechstromfestigkeit | 23.0 °C | 4 V Show Supplier Material materials with Kriechstromfestigkeit of 4 V | UL 746A | (UL) {PLC} |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 6.9 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 6.9 g/10min | ASTM D 1238 | 337°C/6.6 kgf | |
Schrumpfung | 23.0 °C | 0.7 % Show Supplier Material materials with Schrumpfung of 0.7 % | SABIC method | 3.2 mm |
Schrumpfung, diagonal | 23.0 °C | 0.6 % Show Supplier Material materials with Schrumpfung, diagonal of 0.6 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Electronic Components, Air Cabin Interiors, Aircraft Seating, Data Transfer | |
| Availability | Asia,Americas | |
| Processing methods | Drying Temperature: 150°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |