Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.08 g/cm³ Show Supplier Material materials with Dichte of 1.08 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 1.19 % Show Supplier Material materials with Moisture absorption of 1.19 % | ISO 62 | (23°C / 50% RH) |
Wasserabsorption | 23.0 °C | 3.5 % Show Supplier Material materials with Wasserabsorption of 3.5 % | ISO 62-1 | (23°C/saturated) |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 70 MPa Show Supplier Material materials with Biegefestigkeit of 70 MPa | ISO 178 | yield, 2 mm/min |
Biegemodul | 23.0 °C | 1.8 GPa Show Supplier Material materials with Biegemodul of 1.8 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 4 % Show Supplier Material materials with Dehnung of 4 % | ISO 527 | yield, 50 mm/min |
Elastizitätsmodul | 23.0 °C | 2 GPa Show Supplier Material materials with Elastizitätsmodul of 2 GPa | ISO 527 | 1 mm/min |
Hardness, Ball Indentation | 23.0 °C | 80 MPa Show Supplier Material materials with Hardness, Ball Indentation of 80 MPa | ISO 2039-1 | H358/30 |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 45 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 45 kJ/m² | ISO 179/1eA | V-notch Edgew, 23°C, 80*10*4 sp=62mm |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 20 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 20 kJ/m² | ISO 180/1A | 80*10*4, -30°C |
Zugfestigkeit | 23.0 °C | 45 MPa Show Supplier Material materials with Zugfestigkeit of 45 MPa | ISO 527 | break, 50 mm/min |
Thermisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Ball Pressure Test | nan | IEC 60695-10-2 | 125°C +/- 2°C | |
Heat deflection temperature, 0.45 MPa | 175 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 175 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm | |
Koeffizient der thermischen Ausdehnung | 23.0 °C | 9E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 9E-5 1/K | ISO 11359-2 | 23°C to 60°C |
Vicat-Erweichungstemperatur | 180 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 180 °C | ISO 306 | Rate B/120 | |
Wärmeformbeständigkeitstemperatur | 175 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 175 °C | ||
Wärmeleitfähigkeit | 23.0 °C | 0.23 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 0.23 W/(m·K) | ISO 8302 |
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 9E-5 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 9E-5 1/K | ISO 11359-2 | 23°C to 60°C |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzvolumenflussrate | 7 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 7 cm³/10min | ISO 1133 | MVR at 280°C/2.16 kg | |
Schrumpfung | 23.0 °C | 1.4 % Show Supplier Material materials with Schrumpfung of 1.4 % | SABIC method | on tensile bar |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Auto Aftermarket | |
| Availability | Europe | |
| Processing methods | Melt Temperature: 290 to 320.0°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |