Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 99 MPa Show Supplier Material materials with Biegefestigkeit of 99 MPa | ASTM D 790 | yld, 2.6 mm/min, 100 mm span |
Biegemodul | 23.0 °C | 2.4 GPa Show Supplier Material materials with Biegemodul of 2.4 GPa | ASTM D 790 | 2.6 mm/min, 100 mm span |
Dehnung | 23.0 °C | 50 % Show Supplier Material materials with Dehnung of 50 % | ASTM D 638 | brk, Type I, 50 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 106 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 106 J/m | ASTM D 256 | notched, -30°C |
Instrumented Impact, at Peak | 23.0 °C | 40 J Show Supplier Material materials with Instrumented Impact, at Peak of 40 J | ASTM D 3763 | 23°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 176 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 176 kJ/m² | ASTM D 256 | notched, 23°C |
Zugfestigkeit | 23.0 °C | 66 MPa Show Supplier Material materials with Zugfestigkeit of 66 MPa | ASTM D 638 | yld, Type I, 50 mm/min |
Thermisch
Property | Temperature | Value | Comment |
---|---|---|---|
Heat deflection temperature, 0.45 MPa | 204 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 204 °C | ASTM D 648 | 6.4 mm, unannealed | |
Heat deflection temperature, 1.80 MPa | 125 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 125 °C | ASTM D 648 | 6.4 mm, unannealed | |
Koeffizient der thermischen Ausdehnung | 23.0 °C | 9.54E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 9.54E-5 1/K | ASTM E 831 | -20°C to 150°C |
Vicat-Erweichungstemperatur | 245 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 245 °C | ASTM D 1525 | Rate B/50 | |
Wärmeformbeständigkeitstemperatur | 125 - 204 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 125 - 204 °C | ||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 8.1E-5 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 8.1E-5 1/K | ASTM E 831 | -20°C to 150°C |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric constant, 60Hz | 23.0 °C | 3.27 [-] Show Supplier Material materials with Dielectric constant, 60Hz of 3.27 [-] | ASTM D 150 | 50/60 Hz |
Dielektrizitätskonstante, 1 MHz | 23.0 °C | 2.76 [-] Show Supplier Material materials with Dielektrizitätskonstante, 1 MHz of 2.76 [-] | ASTM D 150 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 0.02 [-] | ASTM D 150 | |
Dissipation factor, 50Hz | 23.0 °C | 0.04 [-] Show Supplier Material materials with Dissipation factor, 50Hz of 0.04 [-] | ASTM D 150 | 50/60 Hz |
Durchschlagfestigkeit | 23.0 °C | 25.5 kV/mm Show Supplier Material materials with Durchschlagfestigkeit of 25.5 kV/mm | ASTM D 149 | in oil, 3.2 mm |
Sheet resistivity, ROA | 23.0 °C | 1.70E+16 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1.70E+16 Ω | ASTM D 257 |
Volume resistivity | 23.0 °C | 4.40E+16 Ω·cm Show Supplier Material materials with Volume resistivity of 4.40E+16 Ω·cm | ASTM D 257 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schrumpfung | 23.0 °C | 1.3 % Show Supplier Material materials with Schrumpfung of 1.3 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Wheel Cover, Plumbing, Door Handle, Enclosures | |
Availability | Asia | |
Processing methods | Rear - Zone 1 Temperature: 255 to 295.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |