NORYL™ Resin HNA033 - Europe

Want to keep this datasheet? Save it now in your required format

Description

NORYL™ HNA033 resin is a non-reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This injection moldable grade is heat stabilized and impact modified and was designed to withstand high heat autoclave sterilization <350 cycles. In addition, this grade is US FDA and European Food Contact approved, biocompatible (ISO10993 or USP Class VI), RoHS compliant, and it is subject to SABIC’s Healthcare management of change and formulation lock. NORYL HNA033 resin may be an excellent candidate for applications requiring multiple sterilization cycles such as disposable dental xray mouth guards and surgical stapler components.

Diese Materialdaten wurden von Sabic zur Verfügung gestellt

Alle Daten beziehen sich auf Raumtemperatur soweit nicht anderweitig spezifiziert. SI Einheiten werden verwendt soweit nicht anderweitig spezifiziert.
Äquivalente Standards sind ähnlich zu einem oder mehreren Standards die der Anbieter angegeben hat. Manche äquivalente Standards können strikter sein oder außerhalb der Bedingungen des ursprünglichen Standards.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Anwendungen

Healthcare

Medizinische Ausrüstung

Chirurgische Instrumente

Pharmaindustrie

Materialien von diesem Anbieter

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

Sehen Sie alle Materialen dieses Anbieters

Eigenschaften

Allgemein

Property	Temperature	Value	Comment
Dichte	23.0 °C	1.08 g/cm³ Show Supplier Material materials with Dichte of 1.08 g/cm³	ISO 1183
Moisture absorption	23.0 °C	0.05 % Show Supplier Material materials with Moisture absorption of 0.05 %	ISO 62 \| (23°C / 50% RH)
Relative Dichte	23.0 °C	1.08 [-] Show Supplier Material materials with Relative Dichte of 1.08 [-]	ASTM D 792 \|
Wasserabsorption	23.0 °C	0.15 % Show Supplier Material materials with Wasserabsorption of 0.15 %	ISO 62-1 \| (23°C/saturated)

Mechanisch

Property	Temperature	Value	Comment
Biegefestigkeit	23.0 °C	107 MPa Show Supplier Material materials with Biegefestigkeit of 107 MPa	ISO 178 \| yield, 2 mm/min
Biegemodul	23.0 °C	2.6 GPa Show Supplier Material materials with Biegemodul of 2.6 GPa	ISO 178 \| 2 mm/min
Dehnung	23.0 °C	5.2 % Show Supplier Material materials with Dehnung of 5.2 %	ISO 527 \| yield, 50 mm/min
Elastizitätsmodul	23.0 °C	2.6 GPa Show Supplier Material materials with Elastizitätsmodul of 2.6 GPa	ISO 527 \| 1 mm/min
Impact strength, Izod notched, ASTM	23.0 °C	144 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 144 J/m	ASTM D 256
Instrumented Impact, Total Energy	23.0 °C	47 J Show Supplier Material materials with Instrumented Impact, Total Energy of 47 J	ASTM D 3763 \| 23°C
Schlagfestigkeit, Charpy gekerbt	23.0 °C	15 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 15 kJ/m²	ISO 179/1eA \| V-notch Edgew 80104 sp=62mm, 23°C
Schlagzähigkeit, Izod gekerbt	23.0 °C	10 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 10 kJ/m²	ISO 180/1A \| 80104, -30°C
Zugfestigkeit	23.0 °C	68 MPa Show Supplier Material materials with Zugfestigkeit of 68 MPa	ISO 527 \| yield, 50 mm/min

Thermisch

Property	Temperature	Value	Comment
Heat deflection temperature, 1.80 MPa		141 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 141 °C	ISO 75/Af \| Flatw 80104 sp=64mm
Koeffizient der thermischen Ausdehnung	23.0 °C	7.09E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 7.09E-5 1/K	ISO 11359-2 \| -40°C to 40°C
Vicat-Erweichungstemperatur		162 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 162 °C	ISO 306 \| Rate B/120
Wärmeformbeständigkeitstemperatur		141 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 141 °C
thermischer Ausdehnungskoeffizient, transversal	23.0 °C	6.87E-5 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 6.87E-5 1/K	ISO 11359-2 \| -40°C to 40°C

Rheological Properties

Property	Temperature	Value	Comment
Schmelzmassenflussrate		8.3 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 8.3 g/10min	ASTM D 1238 \| 300°C/5.0 kgf
Schmelzvolumenflussrate		8 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 8 cm³/10min	ISO 1133 \| MVR at 300°C/5.0 kg
Schrumpfung	23.0 °C	0.7 % Show Supplier Material materials with Schrumpfung of 0.7 %	SABIC method \| 3.2 mm

Technological properties

Property
Application areas	Pharmaceutical Packaging & Drug Delivery, Surgical Devices, Surgical Tray, Animal Testing
Availability	Europe,Asia,Americas
Processing methods	Shot to Cylinder Size: 30 to 70.0% Mold Temperature: 75 to 105.0°C Drying Temperature: 105 to 110.0°C Drying Time (Cumulative): 8hrs Front - Zone 3 Temperature: 270 to 310.0°C Back Pressure: 0.3 to 0.7MPa Screw Speed: 20 to 100.0rpm Melt Temperature: 280 to 310.0°C Middle - Zone 2 Temperature: 260 to 305.0°C Rear - Zone 1 Temperature: 250 to 300.0°C Drying Time: 3 to 4.0hrs Maximum Moisture Content: 0.02% Nozzle Temperature: 280 to 310.0°C
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.