Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.21 g/cm³ Show Supplier Material materials with Dichte of 1.21 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.25 % Show Supplier Material materials with Moisture absorption of 0.25 % | ISO 62 | (23°C / 50% RH) |
Relative Dichte | 23.0 °C | 1.2 [-] Show Supplier Material materials with Relative Dichte of 1.2 [-] | ASTM D 792 | |
Wasserabsorption | 23.0 °C | 0.33 % Show Supplier Material materials with Wasserabsorption of 0.33 % | ISO 62-1 | (23°C/saturated) |
Mechanisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Biegefestigkeit | 23.0 °C | 80 MPa Show Supplier Material materials with Biegefestigkeit of 80 MPa | ISO 178 | yield, 2 mm/min | ||
Biegemodul | 23.0 °C | 2.6 GPa Show Supplier Material materials with Biegemodul of 2.6 GPa | ISO 178 | 2 mm/min | ||
Dehnung | 23.0 °C | 50 % Show Supplier Material materials with Dehnung of 50 % | ISO 527 | break, 50 mm/min | ||
Elastizitätsmodul | 23.0 °C | 2.8 GPa Show Supplier Material materials with Elastizitätsmodul of 2.8 GPa | ISO 527 | 1 mm/min | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 93 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 93 J/m | ASTM D 256 | ||
Instrumented Impact, Total Energy | 23.0 °C | 72 J Show Supplier Material materials with Instrumented Impact, Total Energy of 72 J | ASTM D 3763 | 23°C | ||
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 9 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 9 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm, -30°C | ||
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 10 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 10 kJ/m² | ISO 180/1A | 80*10*3, 23°C | ||
Zugfestigkeit | 23.0 °C | 67 MPa Show Supplier Material materials with Zugfestigkeit of 67 MPa | ISO 527 | break, 50 mm/min | ||
Schlagzähigkeit, Charpy ungekerbt | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm, 23°C | ||||
Schlagzähigkeit, Izod ungekerbt | ISO 180/1U | unnotched 80*10*3, 23°C, | ||||
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Ball Pressure Test | nan | IEC 60695-10-2 | 165°C +/- 2°C | |||
Heat deflection temperature, 0.45 MPa | 173 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 173 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |||
Heat deflection temperature, 1.80 MPa | 162 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 162 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 6E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 6E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Vicat-Erweichungstemperatur | 183 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 183 °C | ISO 306 | Rate B/50 | |||
Wärmeformbeständigkeitstemperatur | 162 - 173 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 162 - 173 °C | ||||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 6E-5 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 6E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Entflammbarkeit | Glow Wire Flammability Index 960°C, passes at: 2.5mm IEC 60695-2-12 <br> Glow Wire Flammability Index 960°C, passes at: 2.5mm IEC 60695-2-12 <br> Glow Wire Flammability Index 850°C, passes at: 2mm IEC 60695-2-12 | ||||
Optisch
| Property | Value | Comment |
|---|---|---|
Brechungsindex | 1.61 [-] Show Supplier Material materials with Brechungsindex of 1.61 [-] | ASTM D542 |
Opazität | -0.5 % Show Supplier Material materials with Opazität of -0.5 % | ASTM D 1003 | 2.54 mm |
Transmission | 86 % Show Supplier Material materials with Transmission of 86 % | ASTM D 1003 | 2.54 mm |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 25 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 25 g/10min | ASTM D 1238 | 330°C/2.16 kgf | |
Schmelzvolumenflussrate | 24 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 24 cm³/10min | ISO 1133 | MVR at 330°C/2.16kg | |
Schrumpfung | 23.0 °C | 0.6 % Show Supplier Material materials with Schrumpfung of 0.6 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Forward Lighting, Fog Lamp, Rear/Signal Lighting | |
| Availability | Asia | |
| Processing methods | Back Pressure: 0.3 to 0.7MPa | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |