Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.2 g/cm³ Show Supplier Material materials with Dichte of 1.2 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.25 % Show Supplier Material materials with Moisture absorption of 0.25 % | ISO 62 | (23°C / 50% RH) |
Relative Dichte | 23.0 °C | 1.2 [-] Show Supplier Material materials with Relative Dichte of 1.2 [-] | ASTM D 792 | |
Wasserabsorption | 23.0 °C | 0.25 % Show Supplier Material materials with Wasserabsorption of 0.25 % | ISO 62-1 | (23°C/saturated) |
Mechanisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Biegefestigkeit | 23.0 °C | 105 MPa Show Supplier Material materials with Biegefestigkeit of 105 MPa | ISO 178 | yield, 2 mm/min | ||
Biegemodul | 23.0 °C | 2.4 GPa Show Supplier Material materials with Biegemodul of 2.4 GPa | ISO 178 | 2 mm/min | ||
Dehnung | 23.0 °C | 7 % Show Supplier Material materials with Dehnung of 7 % | ISO 527 | yield, 50 mm/min | ||
Elastizitätsmodul | 23.0 °C | 2.4 GPa Show Supplier Material materials with Elastizitätsmodul of 2.4 GPa | ISO 527 | 1 mm/min | ||
Hardness, Ball Indentation | 23.0 °C | 145 MPa Show Supplier Material materials with Hardness, Ball Indentation of 145 MPa | ISO 2039-1 | H358/30 | ||
Hardness, Rockwell R | 23.0 °C | 125 [-] Show Supplier Material materials with Hardness, Rockwell R of 125 [-] | ISO 2039-2 | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 75 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 75 J/m | ASTM D 256 | notched, -30°C | ||
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 10 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 10 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm, -30°C | ||
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 9 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 9 kJ/m² | ISO 180/1A | notched 80*10*3, -30°C | ||
Zugfestigkeit | 23.0 °C | 60 MPa Show Supplier Material materials with Zugfestigkeit of 60 MPa | ISO 527 | break, 50 mm/min | ||
Impact strength, Izod unnotched, ASTM | ASTM D 4812 | 23°C | ||||
Schlagzähigkeit, Charpy ungekerbt | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm, -30°C | ||||
Schlagzähigkeit, Izod ungekerbt | ISO 180/1U | unnotched 80*10*3, 23°C, | ||||
Thermisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Ball Pressure Test | nan | IEC 60695-10-2 | 125°C +/- 2°C | |
Heat deflection temperature, 0.45 MPa | 150 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 150 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |
Heat deflection temperature, 1.80 MPa | 138 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 138 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Koeffizient der thermischen Ausdehnung | 23.0 °C | 6E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 6E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Vicat-Erweichungstemperatur | 155 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 155 °C | ISO 306 | Rate B/50 | |
Wärmeformbeständigkeitstemperatur | 138 - 150 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 138 - 150 °C | ||
Wärmeleitfähigkeit | 23.0 °C | 0.2 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 0.2 W/(m·K) | ASTM C177 | @ 25 °C |
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 6E-5 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 6E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 37 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 37 g/10min | ASTM D 1238 | 300°C/2.16 kgf | |
Schmelzvolumenflussrate | 85 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 85 cm³/10min | ISO 1133 | MVR at 330°C/2.16kg | |
Schrumpfung | 23.0 °C | 0.6 % Show Supplier Material materials with Schrumpfung of 0.6 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Enclosure/Housing/Cover | |
| Availability | Europe,Asia,Americas | |
| Processing methods | Rear - Zone 1 Temperature: 270 to 315.0°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |