Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.3 g/cm³ Show Supplier Material materials with Dichte of 1.3 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.6 % Show Supplier Material materials with Moisture absorption of 0.6 % | ISO 62 | (23°C / 50% RH) |
Relative Dichte | 23.0 °C | 1.3 [-] Show Supplier Material materials with Relative Dichte of 1.3 [-] | ASTM D 792 |
Sauerstoffindex | 23.0 °C | 45 % Show Supplier Material materials with Sauerstoffindex of 45 % | |
Wasserabsorption | 23.0 °C | 1.75 % Show Supplier Material materials with Wasserabsorption of 1.75 % | ISO 62-1 | (23°C/saturated) |
Mechanisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Biegefestigkeit | 23.0 °C | 123 MPa Show Supplier Material materials with Biegefestigkeit of 123 MPa | ISO 178 | yield, 2 mm/min | ||
Biegemodul | 23.0 °C | 3.1 GPa Show Supplier Material materials with Biegemodul of 3.1 GPa | ISO 178 | 2 mm/min | ||
Dehnung | 23.0 °C | 50 % Show Supplier Material materials with Dehnung of 50 % | ISO 527 | break, 5 mm/min | ||
Elastizitätsmodul | 23.0 °C | 3.1 GPa Show Supplier Material materials with Elastizitätsmodul of 3.1 GPa | ISO 527 | 1 mm/min | ||
Hardness, Ball Indentation | 23.0 °C | 140 MPa Show Supplier Material materials with Hardness, Ball Indentation of 140 MPa | ISO 2039-1 | H358/30 | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 69 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 69 J/m | ASTM D 256 | notched, 23°C | ||
Instrumented Impact, Total Energy | 23.0 °C | 33 J Show Supplier Material materials with Instrumented Impact, Total Energy of 33 J | ASTM D 3763 | 23°C | ||
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 5 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 5 kJ/m² | ISO 180/1A | 80*10*4, -30°C | ||
Zugfestigkeit | 23.0 °C | 78 MPa Show Supplier Material materials with Zugfestigkeit of 78 MPa | ISO 527 | break, 5 mm/min | ||
Impact strength, Izod unnotched, ASTM | ASTM D 4812 | 23°C | ||||
Schlagzähigkeit, Charpy ungekerbt | ISO 179/1eU | Unnotch Edgew 80*10*4 sp=62mm, -30°C | ||||
Schlagzähigkeit, Izod ungekerbt | ISO 180/1U | 80*10*4, 23°C |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Ball Pressure Test | Passes | IEC 60695-10-2 | 125°C +/- 2°C | |||
Glow Wire Ignition Temperature | 850 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 850 °C | IEC 60695-2-13 | 3.0 mm | |||
Heat deflection temperature, 0.45 MPa | 237 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 237 °C | ASTM D 648 | 6.4 mm, unannealed | |||
Heat deflection temperature, 1.80 MPa | 228 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 228 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 5E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 5E-5 1/K | ISO 11359-2 | 23°C to 150°C | ||
Vicat-Erweichungstemperatur | 238 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 238 °C | ISO 306 | Rate B/120 | |||
Wärmeformbeständigkeitstemperatur | 228 - 237 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 228 - 237 °C | ||||
Wärmeleitfähigkeit | 23.0 °C | 0.22 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 0.22 W/(m·K) | ASTM E 1530 | | ||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 5E-5 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 5E-5 1/K | ISO 11359-2 | 23°C to 150°C | ||
Entflammbarkeit | Glow Wire Flammability Index 960°C, passes at: 3.2mm IEC 60695-2-12 <br> Glow Wire Flammability Index 960°C, passes at: 3.2mm IEC 60695-2-12 |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dielektrizitätskonstante, 100 Hz | 23.0 °C | 3.41 [-] Show Supplier Material materials with Dielektrizitätskonstante, 100 Hz of 3.41 [-] | ASTM D 150 |
Dissipation factor, 100Hz | 23.0 °C | 8E-3 [-] Show Supplier Material materials with Dissipation factor, 100Hz of 8E-3 [-] | IEC 60250 |
Dissipation factor, 1MHz | 23.0 °C | 7E-3 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 7E-3 [-] | IEC 60250 |
Dissipation factor, 1kHz | 23.0 °C | 1E-3 [-] Show Supplier Material materials with Dissipation factor, 1kHz of 1E-3 [-] | IEC 60250 |
Dissipation factor, 50Hz | 23.0 °C | 0.03 [-] Show Supplier Material materials with Dissipation factor, 50Hz of 0.03 [-] | IEC 60250 | 50/60 Hz |
Durchschlagfestigkeit | 23.0 °C | 17 kV/mm Show Supplier Material materials with Durchschlagfestigkeit of 17 kV/mm | ASTM D 149 | in oil, 3.2 mm |
Kriechstromfestigkeit | 23.0 °C | 175 V Show Supplier Material materials with Kriechstromfestigkeit of 175 V | IEC 60112 | |
Optisch
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzmassenflussrate | 15.5 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 15.5 g/10min | ASTM D 1238 | 367°C/6.6 kgf | |
Schmelzvolumenflussrate | 8 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 8 cm³/10min | ISO 1133 | MVR at 360°C/5.0 kg | |
Schrumpfung | 23.0 °C | 0.5 % Show Supplier Material materials with Schrumpfung of 0.5 % | SABIC method | 3.2 mm |
Schrumpfung, diagonal | 23.0 °C | 0.5 % Show Supplier Material materials with Schrumpfung, diagonal of 0.5 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Availability | Europe,Asia,Americas | |
Processing methods | Vent Depth: 0.025 to 0.076mm | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |