Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 0.11 g/cm³ Show Supplier Material materials with Dichte of 0.11 g/cm³ | ASTM D 1622 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Druckfestigkeit, transversal | 23.0 °C | 1.7 MPa Show Supplier Material materials with Druckfestigkeit, transversal of 1.7 MPa | ASTM D 1621 |
Elastizitätsmodul | 23.0 °C | 0 GPa Show Supplier Material materials with Elastizitätsmodul of 0 GPa | ASTM D 638 |
Kompressionsmodul | 23.0 °C | 103 MPa Show Supplier Material materials with Kompressionsmodul of 103 MPa | |
Kompressionsmodule, transversal | 23.0 °C | 103 MPa Show Supplier Material materials with Kompressionsmodule, transversal of 103 MPa | ASTM D 1621 |
Scherfestigkeit | 23.0 °C | 1.4 MPa Show Supplier Material materials with Scherfestigkeit of 1.4 MPa | ASTM C 273 |
Schubmodule | 23.0 °C | 0 GPa Show Supplier Material materials with Schubmodule of 0 GPa | ASTM C 273 |
Thermisch
| Property | Value |
|---|---|
Entflammbarkeit | Smoke Density: <10Ds FAR 25.853 <br> OSU peak heat release rate (5 minute test): <55kW/m² FAR 25.853 <br> Smoke Toxicity: PASSES- OEM BSS <br> Vertical Burn at 60 Seconds: PASSES- FAR 25.853 <br> Insulation Radiant Panel: PASSES- FAR 25.856 <br> Smoke Toxicity: PASSES- OEM ABD |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Composite, Sensor | |
| Availability | Europe,Asia,Americas | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |