Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.53 g/cm³ Show Supplier Material materials with Dichte of 1.53 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 0.02 % Show Supplier Material materials with Wasserabsorption of 0.02 % | ISO 62 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 220 MPa Show Supplier Material materials with Biegefestigkeit of 220 MPa | ISO 178 |
Biegemodul | 23.0 °C | 10 GPa Show Supplier Material materials with Biegemodul of 10 GPa | ISO 178 |
Dehnung | 23.0 °C | 2.5 % Show Supplier Material materials with Dehnung of 2.5 % | ISO 527 |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 15 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 15 kJ/m² | ISO 179 |
Zugfestigkeit | 23.0 °C | 155 MPa Show Supplier Material materials with Zugfestigkeit of 155 MPa | ISO 527 |
Thermisch
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 1.80 MPa | 250 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 250 °C | ISO 75 | |
Max. Betriebstemperatur | 250 °C Show Supplier Material materials with Max. Betriebstemperatur of 250 °C | ||
Schmelzpunkt | 280 °C Show Supplier Material materials with Schmelzpunkt of 280 °C | ISO 11357 (10°C/min) | |
Entflammbarkeit | V-0, UL-94 |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dielektrizitätskonstante | 23.0 °C | 4 [-] Show Supplier Material materials with Dielektrizitätskonstante of 4 [-] | IEC 60250 |
Durchschlagfestigkeit | 23.0 °C | 16 kV/mm Show Supplier Material materials with Durchschlagfestigkeit of 16 kV/mm | IEC 60243 |
Kriechstromfestigkeit | 23.0 °C | 125 V Show Supplier Material materials with Kriechstromfestigkeit of 125 V | IEC 60112 |
Verlustfaktor | 23.0 °C | 2E-3 [-] Show Supplier Material materials with Verlustfaktor of 2E-3 [-] | IEC 60250 |
Volume resistivity | 23.0 °C | 2.00E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 2.00E+15 Ω·cm | IEC 60093 |
Technological properties
Property | ||
---|---|---|
Application areas | Can be used in the production of Aluminum Alloy fixture, mixing warter valve, water heater set of water treatment equipment, and other products in the field of high toughness | |
Fillers | 30% Glass Fiber, linear polyphenylene sulfide and elastomer | |
Processing methods | Injection Moulding / Test Specimen Production: Drying: 150°C & 3 hours - Injection Pressure: 30-100 MPa - Injection Molding Melt Temperature: 290-330°C - Injection Molding Mold Temperature: 120-160°C - Limit in-cylinder Retention Time: 300°C/60min or 320°C/30min |