Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.67 g/cm³ Show Supplier Material materials with Dichte of 1.67 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 0.02 % Show Supplier Material materials with Wasserabsorption of 0.02 % | ISO 62 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 265 MPa Show Supplier Material materials with Biegefestigkeit of 265 MPa | ISO 178 |
Biegemodul | 23.0 °C | 14 GPa Show Supplier Material materials with Biegemodul of 14 GPa | ISO 178 |
Dehnung | 23.0 °C | 1.7 % Show Supplier Material materials with Dehnung of 1.7 % | ISO 527 |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 11 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 11 kJ/m² | ISO 179 |
Zugfestigkeit | 23.0 °C | 175 MPa Show Supplier Material materials with Zugfestigkeit of 175 MPa | ISO 527 |
Thermisch
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dielektrizitätskonstante | 23.0 °C | 4 [-] Show Supplier Material materials with Dielektrizitätskonstante of 4 [-] | IEC 60250 |
Durchschlagfestigkeit | 23.0 °C | 16 kV/mm Show Supplier Material materials with Durchschlagfestigkeit of 16 kV/mm | IEC 60243 |
Kriechstromfestigkeit | 23.0 °C | 150 V Show Supplier Material materials with Kriechstromfestigkeit of 150 V | IEC 60112 |
Verlustfaktor | 23.0 °C | 2E-3 [-] Show Supplier Material materials with Verlustfaktor of 2E-3 [-] | IEC 60250 |
Volume resistivity | 23.0 °C | 2.00E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 2.00E+15 Ω·cm | IEC 60093 |
Technological properties
Property | ||
---|---|---|
Application areas | Can be used in electronics,communications,high-frequency heating industrial equipment and measurement, inspection and test equipment such as the need to engage in electrostatic and electromagnetic shielding and other occasions, in order to reduce the source magnetic radiation effect | |
Fillers | 40% Glass Fiber | |
Processing methods | Injection Moulding / Test Specimen Production: Drying: 150°C & 3 hours - Injection Pressure: 30-100 MPa - Injection Molding Melt Temperature: 290-330°C - Injection Molding Mold Temperature: 120-160°C - Limit in-cylinder Retention Time: 300°C/60min or 320°C/30min |