Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.97 g/cm³ Show Supplier Material materials with Dichte of 1.97 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 0.02 % Show Supplier Material materials with Wasserabsorption of 0.02 % | ISO 62 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 225 MPa Show Supplier Material materials with Biegefestigkeit of 225 MPa | ISO 178 |
Biegemodul | 23.0 °C | 21 GPa Show Supplier Material materials with Biegemodul of 21 GPa | ISO 178 |
Dehnung | 23.0 °C | 1 % Show Supplier Material materials with Dehnung of 1 % | ISO 527 |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 7 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 7 kJ/m² | ISO 179 |
Zugfestigkeit | 23.0 °C | 145 MPa Show Supplier Material materials with Zugfestigkeit of 145 MPa | ISO 527 |
Thermisch
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dielektrizitätskonstante | 23.0 °C | 5 [-] Show Supplier Material materials with Dielektrizitätskonstante of 5 [-] | IEC 60250 |
Durchschlagfestigkeit | 23.0 °C | 14 kV/mm Show Supplier Material materials with Durchschlagfestigkeit of 14 kV/mm | IEC 60243 |
Kriechstromfestigkeit | 23.0 °C | 225 V Show Supplier Material materials with Kriechstromfestigkeit of 225 V | IEC 60112 |
Verlustfaktor | 23.0 °C | 1E-3 [-] Show Supplier Material materials with Verlustfaktor of 1E-3 [-] | IEC 60250 |
Volume resistivity | 23.0 °C | 1.60E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 1.60E+15 Ω·cm | IEC 60093 |
Technological properties
Property | ||
---|---|---|
Application areas | Can be used in auto parts such as Fuel Pump Impellers,Reflector Housing,Socket Bases and Air-conditioning PTC parts etc. | |
Fillers | 65% Glass Fiber and Mineral Powder | |
Processing methods | Injection Moulding / Test Specimen Production: Drying: 150°C & 3 hours - Injection Pressure: 30-100 MPa - Injection Molding Melt Temperature: 290-330°C - Injection Molding Mold Temperature: 120-160°C - Limit in-cylinder Retention Time: 300°C/60min or 320°C/30min |