Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Bio-based content | 100.0 % Show Supplier Material materials with Bio-based content of 100.0 % | ||
Dichte | 23 °C | 1.09 g/cm³ Show Supplier Material materials with Dichte of 1.09 g/cm³ | ISO 1183 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegemodul | 23 °C | 5.3 GPa Show Supplier Material materials with Biegemodul of 5.3 GPa | ISO 527-2/2 |
Dehnung | 23 °C | 1.6 % Show Supplier Material materials with Dehnung of 1.6 % | ISO 527-2/50 |
Elastizitätsmodul | 23 °C | 6 GPa Show Supplier Material materials with Elastizitätsmodul of 6 GPa | ISO 527-2/2 |
Schlagzähigkeit, Charpy ungekerbt | 23 °C | 12 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 12 kJ/m² | ISO 179/1eU |
Zugfestigkeit | 23 °C | 45 MPa Show Supplier Material materials with Zugfestigkeit of 45 MPa | ISO 527-2/50 |
Thermisch
Property | Value |
---|---|
Entflammbarkeit | UL94: HB |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzmassenflussrate | 23 °C | 10 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 10 g/10min | ISO 1133, 220°C/5kg |
Technological properties
Property | ||
---|---|---|
Certifications | ||
Fillers | 50% T-Wood Fiber | |
Other | General safety instructions, read also Process instructions: | |
Processing methods | Drying: 2 hours at 105°C Injection moulding machine Temperatures: The below instructions may differ on due to injection speed, machine etc. Read process intructions. |