Eigenschaften
Abmessung
| Property | Value |
|---|---|
Breite | 1500 - 2000 mm Show Supplier Material materials with Breite of 1500 - 2000 mm |
Dicke | 3 - 50 mm Show Supplier Material materials with Dicke of 3 - 50 mm |
Länge | 3000 - 6000 mm Show Supplier Material materials with Länge of 3000 - 6000 mm |
Mechanisch
| Property | Temperature | Value |
|---|---|---|
Charpy impact energy, V-notch | -46.0 °C | 45 J Show Supplier Material materials with Charpy impact energy, V-notch of 45 J |
Dehnung | 23.0 °C | 25 % Show Supplier Material materials with Dehnung of 25 % |
Härte, Brinell | 23.0 °C | 310 [-] Show Supplier Material materials with Härte, Brinell of 310 [-] |
Streckgrenze Rp 0,2 | 23.0 °C | 550 MPa Show Supplier Material materials with Streckgrenze Rp 0,2 of 550 MPa |
Zugfestigkeit | 23.0 °C | 750 - 930 MPa Show Supplier Material materials with Zugfestigkeit of 750 - 930 MPa |
Chemical properties
| Property | Value |
|---|---|
Chrom | 24 - 26 % Show Supplier Material materials with Chrom of 24 - 26 % |
Eisen | Balance |
Kohlenstoff | 0.03 % Show Supplier Material materials with Kohlenstoff of 0.03 % |
Kupfer | 0.5 - 1 % Show Supplier Material materials with Kupfer of 0.5 - 1 % |
Mangan | 1 % Show Supplier Material materials with Mangan of 1 % |
Molybdän | 3 - 4 % Show Supplier Material materials with Molybdän of 3 - 4 % |
Nickel | 6 - 8 % Show Supplier Material materials with Nickel of 6 - 8 % |
Phosphor | 0.03 % Show Supplier Material materials with Phosphor of 0.03 % |
Schwefel | 0.01 % Show Supplier Material materials with Schwefel of 0.01 % |
Silizium | 1 % Show Supplier Material materials with Silizium of 1 % |
Stickstoff | 0.2 - 0.3 % Show Supplier Material materials with Stickstoff of 0.2 - 0.3 % |
Wolfram | 0.5 - 1 % Show Supplier Material materials with Wolfram of 0.5 - 1 % |
Technological properties
| Property | ||
|---|---|---|
| Application areas | It is widely used in oil & gas, hydropower, pressure vessels, pulp & paper, structural components and chemical tankers. | |
| Corrosion properties | High resistance to stress corrosion cracking in halide containing environments, High resistance to pitting and crevice corrosion, High resistance to general corrosion, High resistance to erosion corrosion and corrosion fatigue. PREN ≥ 42 | |
| Heat Treatment | Solution annealing at 1100°C followed by water quenching. | |
| Welding | Very good | |