WL 3.3354 Grade 3.3354 O

Want to keep this datasheet? Save it now in your required format

Description

The alloy is characterised by a good corrosion resistance. It is sea water steady and resistant to saline atmosphere. The Mg content increases the strength, but the cold forming capacity decreases. The material is nature hard, i.e. only by a cold forming and not by a purposeful heat treatment a strength increase can be attained. It is well polishable and anodisable. The splinter-giving machinability becomes better with increasing Mg content, just as the weldability. AlMg5 has the highest Mg content of the standardized AlMg alloys, so it is badly cold formable, but the strength is the highest, so that the employment is possible for statically more highly loaded constructions. The alloy is suitable for a splinter-giving machinig on automats. It possesses sensitivity to intergranular corrosion. By a purposeful heat treatment and/or by additive of Mn or Cr the inclination to the intergranular corrosion can be reduced. Application: In the optics, in the automobile engineering for body parts, in mechanical engineering (turned parts). For joining elements (solid rivets, blind rivets, riveting nuts and screws). In the building industry for carrying constructions as well as in shipbuilding considering the sensitivity to corrosion.

Related Standards

Equivalent Materials

Diese Materialdaten wurden von WIAM,AluKey zur Verfügung gestellt

Alle Daten beziehen sich auf Raumtemperatur soweit nicht anderweitig spezifiziert. SI Einheiten werden verwendt soweit nicht anderweitig spezifiziert.
Äquivalente Standards sind ähnlich zu einem oder mehreren Standards die der Anbieter angegeben hat. Manche äquivalente Standards können strikter sein oder außerhalb der Bedingungen des ursprünglichen Standards.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Eigenschaften

Allgemein

Property	Temperature	Value	Condition	Related Standards	Shape
Dichte		2.64 g/cm³ Show Material materials with Dichte of 2.64 g/cm³	O	WL 3.3354	Wire
	20.0 °C	2.64 g/cm³ Show Material materials with Dichte of 2.64 g/cm³	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire

Mechanisch

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Dehnung	20.0 °C	5.0 % Show Material materials with Dehnung of 5.0 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Wire	A100
	20.0 °C	10.0 % Show Material materials with Dehnung of 10.0 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Wire	A10
	20.0 °C	12.0 % Show Material materials with Dehnung of 12.0 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod	A10
	20.0 °C	14.0 % Show Material materials with Dehnung of 14.0 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod
	20.0 °C	14.0 % Show Material materials with Dehnung of 14.0 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Tube	A10
	20.0 °C	16.0 % Show Material materials with Dehnung of 16.0 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Tube
	20.0 °C	28.0 % Show Material materials with Dehnung of 28.0 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354
	60.0 °C	28.0 % Show Material materials with Dehnung of 28.0 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354
	100.0 °C	32.0 % Show Material materials with Dehnung of 32.0 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354
	140.0 °C	40.0 % Show Material materials with Dehnung of 40.0 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354
	180.0 °C	52.0 % Show Material materials with Dehnung of 52.0 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354
	240.0 °C	64.0 % Show Material materials with Dehnung of 64.0 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354
	300.0 °C	100.0 % Show Material materials with Dehnung of 100.0 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354
	360.0 °C	104.0 % Show Material materials with Dehnung of 104.0 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354
Elastizitätsmodul		71.0 GPa Show Material materials with Elastizitätsmodul of 71.0 GPa	O	WL 3.3354	Wire
	20.0 °C	67.0 - 72.0 GPa Show Material materials with Elastizitätsmodul of 67.0 - 72.0 GPa	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
Härte, Brinell	20.0 °C	55.0 [-] Show Material materials with Härte, Brinell of 55.0 [-]	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Wire
	20.0 °C	60.0 [-] Show Material materials with Härte, Brinell of 60.0 [-]	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod
	20.0 °C	65.0 [-] Show Material materials with Härte, Brinell of 65.0 [-]	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Tube
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m				Typical for Wrought 5000 Series Aluminium
Poissonzahl		0.33 [-] Show Material materials with Poissonzahl of 0.33 [-]				Typical for Wrought 5000 Series Aluminium
Scherfestigkeit	20.0 °C	150.0 MPa Show Material materials with Scherfestigkeit of 150.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Wire
Schubmodule	20.0 °C	27.0 GPa Show Material materials with Schubmodule of 27.0 GPa	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
Zugfestigkeit	20.0 °C	250.0 MPa Show Material materials with Zugfestigkeit of 250.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube
	20.0 °C	270.0 MPa Show Material materials with Zugfestigkeit of 270.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Wire
	20.0 °C	280.0 MPa Show Material materials with Zugfestigkeit of 280.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354
	100.0 °C	275.0 MPa Show Material materials with Zugfestigkeit of 275.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354
	140.0 °C	235.0 MPa Show Material materials with Zugfestigkeit of 235.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354
	180.0 °C	200.0 MPa Show Material materials with Zugfestigkeit of 200.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354
	240.0 °C	140.0 MPa Show Material materials with Zugfestigkeit of 140.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354
	300.0 °C	100.0 MPa Show Material materials with Zugfestigkeit of 100.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354
	360.0 °C	55.0 MPa Show Material materials with Zugfestigkeit of 55.0 MPa	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354

Thermisch

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Koeffizient der thermischen Ausdehnung	-50.0 °C	2.25e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.25e-05 1/K	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
	20 °C	2.31e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.31e-05 1/K	O	WL 3.3354	Wire
	100 °C	2.31e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.31e-05 1/K	O	WL 3.3354	Wire
	100.0 °C	2.41e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.41e-05 1/K	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
	200.0 °C	2.51e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.51e-05 1/K	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
	300.0 °C	2.61e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.61e-05 1/K	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
Max. Betriebstemperatur		150.0 °C Show Material materials with Max. Betriebstemperatur of 150.0 °C				Typical for Wrought 5000 Series Aluminium
Schmelzpunkt		565.0 - 640.0 °C Show Material materials with Schmelzpunkt of 565.0 - 640.0 °C	O	WL 3.3354	Wire
Spezifische Wärmekapazität		904.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 904.0 J/(kg·K)	O	WL 3.3354	Wire
	20.0 °C	904.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 904.0 J/(kg·K)	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
Wärmeleitfähigkeit	20.0 °C	110.0 - 140.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 110.0 - 140.0 W/(m·K)	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire

Elektrisch

Property	Temperature	Value	Condition	Related Standards	Shape
Elektrische Leitfähigkeit	20.0 °C	15000000.0 - 19000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 15000000.0 - 19000000.0 S/m	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
spezifischer Widerstand		5.26e-08 - 6.67e-08 Ω·m Show Material materials with spezifischer Widerstand of 5.26e-08 - 6.67e-08 Ω·m	O	WL 3.3354	Wire

Chemical properties

Property	Value	Condition	Related Standards	Shape
Chrom	0.2 % Show Material materials with Chrom of 0.2 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
Eisen	0.5 % Show Material materials with Eisen of 0.5 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
	0.50 % Show Material materials with Eisen of 0.50 %	O	WL 3.3354	Wire
Kupfer	0.1 % Show Material materials with Kupfer of 0.1 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
Magnesium	4.5 - 5.6 % Show Material materials with Magnesium of 4.5 - 5.6 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
Mangan	0.1 - 0.6 % Show Material materials with Mangan of 0.1 - 0.6 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
Silizium	0.4 % Show Material materials with Silizium of 0.4 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
Titan	0.2 Show Material materials with Titan of 0.2	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire
Zink	0.2 % Show Material materials with Zink of 0.2 %	O	DIN 1725-1, EN 573-3, EN 573-4, WL 3.3354	Rod, Tube, Wire

Technological properties

Property

Workability

Good workability.