Allgemein
| Property | Value | Comment |
|---|---|---|
Dichte | 2.75 - 2.84 g/cm³ Show Material materials with Dichte of 2.75 - 2.84 g/cm³ | Typical for Wrought 2000 Series Aluminium |
Mechanisch
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Dehnung | 20.0 °C | 3.0 % Show Material materials with Dehnung of 3.0 % | T652 | WL 3.1254-1 | Forging | Transverse |
20.0 °C | 4.0 % Show Material materials with Dehnung of 4.0 % | T652 | WL 3.1254-1 | Forging | Transverse | |
20.0 °C | 5.0 % Show Material materials with Dehnung of 5.0 % | T652 | WL 3.1254-1 | Forging | Transverse | |
20.0 °C | 6.0 % Show Material materials with Dehnung of 6.0 % | T652 | WL 3.1254-1 | Forging | ||
20.0 °C | 7.0 % Show Material materials with Dehnung of 7.0 % | T652 | WL 3.1254-1 | Forging | ||
20.0 °C | 8.0 % Show Material materials with Dehnung of 8.0 % | T652 | WL 3.1254-1 | Forging | Transverse | |
20.0 °C | 8.0 % Show Material materials with Dehnung of 8.0 % | T652 | WL 3.1254-1 | Forging | ||
Elastizitätsmodul | 70.0 - 73.0 GPa Show Material materials with Elastizitätsmodul of 70.0 - 73.0 GPa | Typical for Wrought 2000 Series Aluminium | ||||
Härte, Brinell | 20.0 °C | 130.0 [-] Show Material materials with Härte, Brinell of 130.0 [-] | T652 | WL 3.1254-1 | Forging | Transverse |
20.0 °C | 130.0 [-] Show Material materials with Härte, Brinell of 130.0 [-] | T652 | WL 3.1254-1 | Forging | ||
Plane-Strain Fracture Toughnes | 20.0 °C | 19.9 - 31.6 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 19.9 - 31.6 MPa·√m | T652 | WL 3.1254-1 | ||
20.0 °C | 19.9 - 24.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 19.9 - 24.0 MPa·√m | T652 | WL 3.1254-1 | |||
20.0 °C | 19.9 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 19.9 MPa·√m | T652 | WL 3.1254-1 | |||
20.0 °C | 24.0 - 31.6 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 24.0 - 31.6 MPa·√m | T652 | WL 3.1254-1 | |||
20.0 °C | 24.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 24.0 MPa·√m | T652 | WL 3.1254-1 | |||
20.0 °C | 31.6 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 31.6 MPa·√m | T652 | WL 3.1254-1 | |||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | Typical for Wrought 2000 Series Aluminium | ||||
Schubmodule | 26.0 - 27.5 GPa Show Material materials with Schubmodule of 26.0 - 27.5 GPa | Typical for Wrought 2000 Series Aluminium | ||||
Zugfestigkeit | 20.0 °C | 395.0 MPa Show Material materials with Zugfestigkeit of 395.0 MPa | T652 | WL 3.1254-1 | Forging | Transverse |
20.0 °C | 400.0 MPa Show Material materials with Zugfestigkeit of 400.0 MPa | T652 | WL 3.1254-1 | Forging | Transverse | |
20.0 °C | 405.0 MPa Show Material materials with Zugfestigkeit of 405.0 MPa | T652 | WL 3.1254-1 | Forging | Transverse | |
20.0 °C | 405.0 MPa Show Material materials with Zugfestigkeit of 405.0 MPa | T652 | WL 3.1254-1 | Forging | ||
20.0 °C | 415.0 MPa Show Material materials with Zugfestigkeit of 415.0 MPa | T652 | WL 3.1254-1 | Forging | Transverse | |
20.0 °C | 415.0 MPa Show Material materials with Zugfestigkeit of 415.0 MPa | T652 | WL 3.1254-1 | Forging | ||
20.0 °C | 420.0 MPa Show Material materials with Zugfestigkeit of 420.0 MPa | T652 | WL 3.1254-1 | Forging | Transverse | |
20.0 °C | 420.0 MPa Show Material materials with Zugfestigkeit of 420.0 MPa | T652 | WL 3.1254-1 | Forging | ||
20.0 °C | 425.0 MPa Show Material materials with Zugfestigkeit of 425.0 MPa | T652 | WL 3.1254-1 | Forging | Transverse | |
20.0 °C | 430.0 MPa Show Material materials with Zugfestigkeit of 430.0 MPa | T652 | WL 3.1254-1 | Forging | Transverse | |
20.0 °C | 430.0 MPa Show Material materials with Zugfestigkeit of 430.0 MPa | T652 | WL 3.1254-1 | Forging | ||
20.0 °C | 435.0 MPa Show Material materials with Zugfestigkeit of 435.0 MPa | T652 | WL 3.1254-1 | Forging | Transverse | |
20.0 °C | 435.0 MPa Show Material materials with Zugfestigkeit of 435.0 MPa | T652 | WL 3.1254-1 | Forging | ||
20.0 °C | 440.0 MPa Show Material materials with Zugfestigkeit of 440.0 MPa | T652 | WL 3.1254-1 | Forging | Transverse | |
20.0 °C | 440.0 MPa Show Material materials with Zugfestigkeit of 440.0 MPa | T652 | WL 3.1254-1 | Forging | ||
20.0 °C | 450.0 MPa Show Material materials with Zugfestigkeit of 450.0 MPa | T652 | WL 3.1254-1 | Forging | Transverse |
Thermisch
| Property | Value | Comment |
|---|---|---|
Koeffizient der thermischen Ausdehnung | 1.6e-05 - 2.4e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.6e-05 - 2.4e-05 1/K | Typical for Wrought 2000 Series Aluminium |
Schmelzpunkt | 500.0 - 650.0 °C Show Material materials with Schmelzpunkt of 500.0 - 650.0 °C | Typical for Wrought 2000 Series Aluminium |
Spezifische Wärmekapazität | 816.0 - 963.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 816.0 - 963.0 J/(kg·K) | Typical for Wrought 2000 Series Aluminium |
Wärmeleitfähigkeit | 112.0 - 251.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 112.0 - 251.0 W/(m·K) | Typical for Wrought 2000 Series Aluminium |
Elektrisch
| Property | Value | Comment |
|---|---|---|
Elektrische Leitfähigkeit | 18000000.0 - 30000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 18000000.0 - 30000000.0 S/m | Typical for Wrought 2000 Series Aluminium |
spezifischer Widerstand | 3.4e-08 - 6e-08 Ω·m Show Material materials with spezifischer Widerstand of 3.4e-08 - 6e-08 Ω·m | Typical for Wrought 2000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chrom | 0.1 Show Material materials with Chrom of 0.1 | T652 | WL 3.1254-1 | Forging |
Eisen | 0.3 Show Material materials with Eisen of 0.3 | T652 | WL 3.1254-1 | Forging |
Kupfer | 3.9 - 5.0 % Show Material materials with Kupfer of 3.9 - 5.0 % | T652 | WL 3.1254-1 | Forging |
Magnesium | 0.2 - 0.8 % Show Material materials with Magnesium of 0.2 - 0.8 % | T652 | WL 3.1254-1 | Forging |
Mangan | 0.4 - 1.2 % Show Material materials with Mangan of 0.4 - 1.2 % | T652 | WL 3.1254-1 | Forging |
Silizium | 0.5 - 1.2 % Show Material materials with Silizium of 0.5 - 1.2 % | T652 | WL 3.1254-1 | Forging |
Titan | 0.15 Show Material materials with Titan of 0.15 | T652 | WL 3.1254-1 | Forging |
Zink | 0.25 Show Material materials with Zink of 0.25 | T652 | WL 3.1254-1 | Forging |
Technological properties
| Property | ||
|---|---|---|
| Workability | Moderate Workability | |