Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Dichte | 20.0 °C | 4.45 g/cm³ Show Material materials with Dichte of 4.45 g/cm³ | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging, Rod |
Mechanisch
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Dehnung | 20.0 °C | 6.0 % Show Material materials with Dehnung of 6.0 % | Artificially Aged | DIN 17851, DIN 17864, WL 3.7154-1 | Forging, Rod | |
Elastizitätsmodul | 20.0 °C | 125.0 GPa Show Material materials with Elastizitätsmodul of 125.0 GPa | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging, Rod | |
Flächenreduzierung | 20.0 °C | 15.0 % Show Material materials with Flächenreduzierung of 15.0 % | Artificially Aged | DIN 17851, DIN 17864, WL 3.7154-1 | Forging, Rod | |
Plane-Strain Fracture Toughnes | 20.0 °C | 64.8 - 74.9 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 64.8 - 74.9 MPa·√m | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging | |
20.0 °C | 64.8 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 64.8 MPa·√m | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging | ||
20.0 °C | 64.8 - 67.9 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 64.8 - 67.9 MPa·√m | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging | ||
20.0 °C | 64.8 - 68.3 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 64.8 - 68.3 MPa·√m | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging | ||
20.0 °C | 67.9 - 74.9 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 67.9 - 74.9 MPa·√m | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging | ||
20.0 °C | 67.9 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 67.9 MPa·√m | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging | ||
20.0 °C | 67.9 - 68.3 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 67.9 - 68.3 MPa·√m | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging | ||
20.0 °C | 68.3 - 74.9 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 68.3 - 74.9 MPa·√m | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging | ||
20.0 °C | 68.3 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 68.3 MPa·√m | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging | ||
20.0 °C | 74.9 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 74.9 MPa·√m | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging | ||
Schubmodule | 20.0 °C | 47.0 GPa Show Material materials with Schubmodule of 47.0 GPa | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging, Rod | |
Streckgrenze | 20.0 °C | 880.0 MPa Show Material materials with Streckgrenze of 880.0 MPa | Artificially Aged | DIN 17851, DIN 17864, WL 3.7154-1 | Forging, Rod | RP02 |
20.0 °C | 940.0 - 962.0 MPa Show Material materials with Streckgrenze of 940.0 - 962.0 MPa | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging | ||
20.0 °C | 940.0 MPa Show Material materials with Streckgrenze of 940.0 MPa | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging | ||
20.0 °C | 940.0 - 967.0 MPa Show Material materials with Streckgrenze of 940.0 - 967.0 MPa | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging | ||
20.0 °C | 962.0 MPa Show Material materials with Streckgrenze of 962.0 MPa | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging | ||
20.0 °C | 962.0 - 967.0 MPa Show Material materials with Streckgrenze of 962.0 - 967.0 MPa | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging | ||
20.0 °C | 967.0 MPa Show Material materials with Streckgrenze of 967.0 MPa | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging | ||
Zugfestigkeit | 20.0 °C | 950.0 MPa Show Material materials with Zugfestigkeit of 950.0 MPa | Artificially Aged | DIN 17851, DIN 17864, WL 3.7154-1 | Forging, Rod |
Thermisch
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 7.099999999999997e-06 - 9.699999999999999e-06 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 7.099999999999997e-06 - 9.699999999999999e-06 1/K | Typical for Titanium Beta Alloy | ||||
Schmelzpunkt | 1550.0 - 1815.0 °C Show Material materials with Schmelzpunkt of 1550.0 - 1815.0 °C | Typical for Titanium Beta Alloy | ||||
Spezifische Wärmekapazität | 20.0 °C | 540.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 540.0 J/(kg·K) | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging, Rod | |
Wärmeleitfähigkeit | 20.0 °C | 4.2 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 4.2 W/(m·K) | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging, Rod |
Chemical properties
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Aluminium | 5.7 - 6.3 % Show Material materials with Aluminium of 5.7 - 6.3 % | Artificially Aged | DIN 17851, DIN 17864, WL 3.7154-1 | Forging, Rod |
Eisen | 0.2 Show Material materials with Eisen of 0.2 | Artificially Aged | DIN 17851, DIN 17864, WL 3.7154-1 | Forging, Rod |
Kohlenstoff | 0.08 Show Material materials with Kohlenstoff of 0.08 | Artificially Aged | DIN 17851, DIN 17864, WL 3.7154-1 | Forging |
Molybdän | 0.25 - 0.75 % Show Material materials with Molybdän of 0.25 - 0.75 % | Artificially Aged | DIN 17851, DIN 17864, WL 3.7154-1 | Forging, Rod |
Sauerstoff | 0.19 Show Material materials with Sauerstoff of 0.19 | Artificially Aged | DIN 17851, DIN 17864, WL 3.7154-1 | Forging, Rod |
Silizium | 0.1 - 0.4 % Show Material materials with Silizium of 0.1 - 0.4 % | Artificially Aged | DIN 17851, DIN 17864, WL 3.7154-1 | Forging, Rod |
Stickstoff | 0.05 Show Material materials with Stickstoff of 0.05 | Artificially Aged | DIN 17851, DIN 17864, WL 3.7154-1 | Forging, Rod |
Titan | 85.6 % Show Material materials with Titan of 85.6 % | Artificially Aged | DIN 17851, DIN 17864, WL 3.7154-1 | Forging, Rod |
Wasserstoff | 0.015 Show Material materials with Wasserstoff of 0.015 | Artificially Aged | DIN 17851, DIN 17864, WL 3.7154-1 | Forging |
Zirkonium | 4.0 - 6.0 % Show Material materials with Zirkonium of 4.0 - 6.0 % | Artificially Aged | DIN 17851, DIN 17864, WL 3.7154-1 | Forging, Rod |