DIN 17851 Grade TiAl6V6Sn2 Annealed

Want to keep this datasheet? Save it now in your required format

Description

Chemical composition: DIN 17851 TiAl6V6Sn2 with the material number 3.7175 (see also TiAl6V6Sn2, material number 3.7174, according to the Werkstoff-Leistungsblatt der Deutschen Luftfahrt WL 3.7174) belongs to the hardenable alpha + beta-titanium alloys. It is similar to the 3.7164 or 3.7165 (TiAl6V4), yet the beta-phase is more stable and the material shows higher strength. It possesses good resistance to corrosion, it is well forgeable, and the long-term application temperature is approximately 350 °C. Processing properties: Formability: limited (cold forming), good (hot forming) Weldability: limited (embrittlement of the welding and heat affected zone by transformation hardening, electron-beam welding) (Werkstoff-Leistungsblatt der Deutschen Luftfahrt WL: material specification of the German aviation)

Related Standards

Equivalent Materials

Diese Materialdaten wurden von WIAM zur Verfügung gestellt

Alle Daten beziehen sich auf Raumtemperatur soweit nicht anderweitig spezifiziert. SI Einheiten werden verwendt soweit nicht anderweitig spezifiziert.
Äquivalente Standards sind ähnlich zu einem oder mehreren Standards die der Anbieter angegeben hat. Manche äquivalente Standards können strikter sein oder außerhalb der Bedingungen des ursprünglichen Standards.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Eigenschaften

Allgemein

Property	Temperature	Value	Condition	Related Standards	Shape
Dichte	20.0 °C	4.54 g/cm³ Show Material materials with Dichte of 4.54 g/cm³	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod, Plate, Flat

Mechanisch

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Dehnung	20.0 °C	6.0 % Show Material materials with Dehnung of 6.0 %	Annealed	WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860	Plate
	20.0 °C	7.0 % Show Material materials with Dehnung of 7.0 %	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod	Transverse
	20.0 °C	8.0 % Show Material materials with Dehnung of 8.0 %	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod, Plate
Elastizitätsmodul	20.0 °C	116.0 GPa Show Material materials with Elastizitätsmodul of 116.0 GPa	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod, Plate, Flat
	200.0 °C	108.0 GPa Show Material materials with Elastizitätsmodul of 108.0 GPa	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod, Plate, Flat
	400.0 °C	99.0 GPa Show Material materials with Elastizitätsmodul of 99.0 GPa	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod, Plate, Flat
Flächenreduzierung	20.0 °C	15.0 % Show Material materials with Flächenreduzierung of 15.0 %	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging	Transverse
	20.0 °C	20.0 % Show Material materials with Flächenreduzierung of 20.0 %	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod, Plate
Härte, Brinell	20.0 °C	320.0 Show Material materials with Härte, Brinell of 320.0	Annealed	DIN 17862, WL 3.7174-1, DIN 17851, DIN 17864, DIN 17860	Rod
Plane-Strain Fracture Toughnes	20.0 °C	46.1 - 54.8 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 46.1 - 54.8 MPa·√m	Annealed	WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860	Plate
	20.0 °C	46.1 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 46.1 MPa·√m	Annealed	WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860	Plate
	20.0 °C	54.8 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 54.8 MPa·√m	Annealed	WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860	Plate
	20.0 °C	62.7 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 62.7 MPa·√m	Annealed	WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860	Rod, Forging
	20.0 °C	62.7 - 71.9 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 62.7 - 71.9 MPa·√m	Annealed	WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860	Rod, Forging
	20.0 °C	62.7 - 70.8 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 62.7 - 70.8 MPa·√m	Annealed	WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860	Rod, Forging
	20.0 °C	70.8 - 71.9 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 70.8 - 71.9 MPa·√m	Annealed	WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860	Rod, Forging
	20.0 °C	70.8 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 70.8 MPa·√m	Annealed	WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860	Rod, Forging
	20.0 °C	71.9 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 71.9 MPa·√m	Annealed	WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860	Rod, Forging
Schubmodule	20.0 °C	45.0 GPa Show Material materials with Schubmodule of 45.0 GPa	Annealed	WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860	Forging, Plate, Rod, Flat
Zugfestigkeit	20.0 °C	1000.0 MPa Show Material materials with Zugfestigkeit of 1000.0 MPa	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod	Transverse
	20.0 °C	1000.0 MPa Show Material materials with Zugfestigkeit of 1000.0 MPa	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod, Plate
	20.0 °C	1030.0 MPa Show Material materials with Zugfestigkeit of 1030.0 MPa	Annealed	WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860	Plate
	20.0 °C	1070.0 MPa Show Material materials with Zugfestigkeit of 1070.0 MPa	Annealed	WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860	Flat
	20.0 °C	1140.0 MPa Show Material materials with Zugfestigkeit of 1140.0 MPa	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860
	100.0 °C	1065.0 MPa Show Material materials with Zugfestigkeit of 1065.0 MPa	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860
	200.0 °C	990.0 MPa Show Material materials with Zugfestigkeit of 990.0 MPa	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860
	300.0 °C	930.0 MPa Show Material materials with Zugfestigkeit of 930.0 MPa	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860
	400.0 °C	900.0 MPa Show Material materials with Zugfestigkeit of 900.0 MPa	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860

Thermisch

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Koeffizient der thermischen Ausdehnung		7.699999999999999e-06 - 1e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 7.699999999999999e-06 - 1e-05 1/K				Typical for Titanium Alpha Beta Alloy
Schmelzpunkt		1500.0 - 1750.0 °C Show Material materials with Schmelzpunkt of 1500.0 - 1750.0 °C				Typical for Titanium Alpha Beta Alloy
Spezifische Wärmekapazität		370.0 - 674.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 370.0 - 674.0 J/(kg·K)				Typical for Titanium Alpha Beta Alloy
Wärmeleitfähigkeit	20.0 °C	6.5 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 6.5 W/(m·K)	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod, Plate, Flat

Elektrisch

Property	Temperature	Value	Condition	Related Standards	Shape
spezifischer Widerstand	20.0 °C	1.57e-06 Ω·m Show Material materials with spezifischer Widerstand of 1.57e-06 Ω·m	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod, Plate, Flat

Chemical properties

Property	Value	Condition	Related Standards	Shape
Aluminium	5.0 - 6.0 % Show Material materials with Aluminium of 5.0 - 6.0 %	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod, Plate, Flat
Eisen	0.35 - 1.0 % Show Material materials with Eisen of 0.35 - 1.0 %	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod, Plate, Flat
Kohlenstoff	0.05 Show Material materials with Kohlenstoff of 0.05	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod, Plate, Flat
Kupfer	0.35 - 1.0 % Show Material materials with Kupfer of 0.35 - 1.0 %	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod, Plate, Flat
Sauerstoff	0.2 Show Material materials with Sauerstoff of 0.2	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod, Plate, Flat
Stickstoff	0.04 Show Material materials with Stickstoff of 0.04	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod, Plate, Flat
Titan	82.8 % Show Material materials with Titan of 82.8 %	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod, Plate, Flat
Vanadium	5.0 - 6.0 % Show Material materials with Vanadium of 5.0 - 6.0 %	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod, Plate, Flat
Wasserstoff	0.015 Show Material materials with Wasserstoff of 0.015	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod
Zinn	1.5 - 2.5 % Show Material materials with Zinn of 1.5 - 2.5 %	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod, Plate, Flat