General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Densidad | 2.67 g/cm³ Show Material materials with Densidad of 2.67 g/cm³ | O | AA Standards, ASTM B209 |
Mecánica
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Bending Fatigue Strength | 110.0 MPa Show Material materials with Bending Fatigue Strength of 110.0 MPa | O | AA Standards | |
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Dureza Brinell | 47.0 [-] Show Material materials with Dureza Brinell of 47.0 [-] | O | AA Standards | |
Módulo de cizallamiento | 26.0 - 26.5 GPa Show Material materials with Módulo de cizallamiento of 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | ||
Módulo elástico | 70.0 GPa Show Material materials with Módulo elástico of 70.0 GPa | O | AA Standards, ASTM B209 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Resistencia a la tracción | 170.0 - 215.0 MPa Show Material materials with Resistencia a la tracción of 170.0 - 215.0 MPa | O | AA Standards, ASTM B209 | |
195.0 MPa Show Material materials with Resistencia a la tracción of 195.0 MPa | O | AA Standards |
Aplicaciones térmicas
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Calor específico | 879.0 - 963.0 J/(kg·K) Show Material materials with Calor específico of 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium | |||
Coeficiente de dilatación térmica | 20 °C | 2.38e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.38e-05 1/K | O | AA Standards, ASTM B209 | |
100 °C | 2.38e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.38e-05 1/K | O | AA Standards, ASTM B209 | ||
Conductividad térmica | 138 W/(m·K) Show Material materials with Conductividad térmica of 138 W/(m·K) | O | AA Standards, ASTM B209 | ||
Temperatura de fusión | 605.0 - 650.0 °C Show Material materials with Temperatura de fusión of 605.0 - 650.0 °C | O | AA Standards, ASTM B209 | ||
Temperatura máx. de funcionamiento | 150.0 °C Show Material materials with Temperatura máx. de funcionamiento of 150.0 °C | Typical for Wrought 5000 Series Aluminium |
Eléctrico
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Conductividad eléctrica | 20000000.0 S/m Show Material materials with Conductividad eléctrica of 20000000.0 S/m | O | AA Standards, ASTM B209 |
Resistividad eléctrica | 5e-08 Ω·m Show Material materials with Resistividad eléctrica of 5e-08 Ω·m | O | AA Standards, ASTM B209 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Cobre | 0.04 % Show Material materials with Cobre of 0.04 % | O | AA Standards, ASTM B209 |
Cromo | 0.15 - 0.35 % Show Material materials with Cromo of 0.15 - 0.35 % | O | AA Standards, ASTM B209 |
Magnesio | 2.2 - 2.8 % Show Material materials with Magnesio of 2.2 - 2.8 % | O | AA Standards, ASTM B209 |
Manganeso | 0.01 % Show Material materials with Manganeso of 0.01 % | O | AA Standards, ASTM B209 |
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % | O | AA Standards, ASTM B209 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: limited brazing | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O, H32), sufficient (H34, H36, H38) | |
| Workability | general (condition): good (O), acceptable (H32, H34), poor(H36, H38) | |