General
Property | Temperature | Value |
---|---|---|
Densidad | 20.0 °C | 8.9 g/cm³ Show Material materials with Densidad of 8.9 g/cm³ |
Medidas
Property | Value |
---|---|
Dimensions | Durchmesser |
Mecánica
Property | Temperature | Value |
---|---|---|
Dureza Brinell | 20.0 °C | 65 - 95 [-] Show Material materials with Dureza Brinell of 65 - 95 [-] |
Dureza Vickers | 20.0 °C | 70 - 100 [-] Show Material materials with Dureza Vickers of 70 - 100 [-] |
Elongación | 20.0 °C | 25 % Show Material materials with Elongación of 25 % |
Elongation A100 | 20.0 °C | 20 % Show Material materials with Elongation A100 of 20 % |
Límite elástico Rp 0,2 | 20.0 °C | 140 MPa Show Material materials with Límite elástico Rp 0,2 of 140 MPa |
Resistencia a la tracción | 20.0 °C | 250 MPa Show Material materials with Resistencia a la tracción of 250 MPa |
Aplicaciones térmicas
Property | Value |
---|---|
Temperatura de fusión | 1038 - 1082 °C Show Material materials with Temperatura de fusión of 1038 - 1082 °C |
Chemical properties
Property | Value |
---|---|
Fósforo | 0.15 - 0.25 % Show Material materials with Fósforo of 0.15 - 0.25 % |
Níquel | 0.8 - 1.2 % Show Material materials with Níquel of 0.8 - 1.2 % |
Otro | Rest Cu, total 0.1 |
Technological properties
Property | ||
---|---|---|
Brazing | hard brazing : good to medium, soft brazing: good | |
Workability | Cold forming degree between anneals: max. 75 % (lösungsgeglüht), general (condition): good (solution annealed) |