Property | Value | Comment |
---|---|---|
Dureza Vickers | 200 - 230 [-] Show Supplier Material materials with Dureza Vickers of 200 - 230 [-] | Typical values for thickness 0.65 mm |
Elongación | 10 % Show Supplier Material materials with Elongación of 10 % | min. | for thickness 0.65 mm | Transverse | A80 | Guaranteed |
25 - 35 % Show Supplier Material materials with Elongación of 25 - 35 % | for thickness 0.65 mm | Transverse | A80 | Typical values | |
Límite elástico | 400 MPa Show Supplier Material materials with Límite elástico of 400 MPa | min. | Guaranteed | Transverse |
470 - 510 MPa Show Supplier Material materials with Límite elástico of 470 - 510 MPa | Typical values | Transverse | |
Resistencia a la tracción | 450 MPa Show Supplier Material materials with Resistencia a la tracción of 450 MPa | min. | Guaranteed |
590 - 630 MPa Show Supplier Material materials with Resistencia a la tracción of 590 - 630 MPa | Typical values | |
Yield to strength ratio | 0.77 - 0.82 [-] Show Supplier Material materials with Yield to strength ratio of 0.77 - 0.82 [-] | Typical values |
Magnético
Property | Value | Comment |
---|---|---|
Polarización garantizada | 1.5 [-] Show Supplier Material materials with Polarización garantizada of 1.5 [-] | min. | for thickness 0.65 mm | in DC at 5000 A/m |
1.8 [-] Show Supplier Material materials with Polarización garantizada of 1.8 [-] | min. | for thickness 0.65 mm | in DC at 15000 A/m | |
Polarización normal | 1.64 [-] Show Supplier Material materials with Polarización normal of 1.64 [-] | min. | for thickness 0.65 mm | in DC at 5000 A/m |
1.84 [-] Show Supplier Material materials with Polarización normal of 1.84 [-] | min. | for thickness 0.65 mm | in DC at 15000 A/m |
Technological properties
Property | ||
---|---|---|
Application areas | Cold rolled pole sheet grade is designed for large high-speed machines because of its excellent combination of mechanical strength and magnetic performance. | |
Other | These properties are obtained without heat treatment after stamping. The material as supplied possesses all the required magnetic properties. |