| Property | Temperature | Value | Testing Standard |
|---|---|---|---|
Densidad | 25 °C | 1.02 g/cm³ Show Supplier Material materials with Densidad of 1.02 g/cm³ | ISO 1183-1 |
Mecánica
| Property | Temperature | Value | Testing Standard | Comment |
|---|---|---|---|---|
Elongación | 15 % Show Supplier Material materials with Elongación of 15 % | ISO 527-1/2 | min. | 50 mm/min | |
Hardness, Ball Indentation | 81 MPa Show Supplier Material materials with Hardness, Ball Indentation of 81 MPa | ISO 2039-1 | ||
Límite elástico | 38 MPa Show Supplier Material materials with Límite elástico of 38 MPa | ISO 527-1/2 | 50 mm/min | |
Módulo de flexión | 1.9 GPa Show Supplier Material materials with Módulo de flexión of 1.9 GPa | ISO 178 | 2 mm/min | |
Módulo elástico | 1.9 GPa Show Supplier Material materials with Módulo elástico of 1.9 GPa | ISO 527-1/2 | 1 mm/min | |
Resistencia a la flexión | 66 MPa Show Supplier Material materials with Resistencia a la flexión of 66 MPa | ISO 178 | 2 mm/min | |
Resistencia al choque, ensayo Charpy entallado | -30 °C | 21 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 21 kJ/m² | ISO 179-1eA | |
23 °C | 31 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 31 kJ/m² | ISO 179-1eA | ||
Resistencia al choque, ensayo Izod entallado | -30 °C | 20 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 20 kJ/m² | ISO 180-1A | |
23 °C | 25 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 25 kJ/m² | ISO 180-1A |
Aplicaciones térmicas
| Property | Value | Testing Standard | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 0.0001 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 0.0001 1/K | ISO 11359-1/2 | 23 to 55°C | ||
Temperatura de reblandecimiento Vicat | 95 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 95 °C | ISO 306 | 50 N | 50°C/h | ||
97 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 97 °C | ISO 306 | 50 N | 120°C/h | |||
Inflamabilidad | At thickness 1.6 mm UL 94: HB. Burning rate US-FMVSS (2mm): < 40 mm/min according to ISO 3795 | ||||
Rheological Properties
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Contracción | 0.6 - 0.7 % Show Supplier Material materials with Contracción of 0.6 - 0.7 % | ISO 294-4 | 60x60x2 mm |
0.6 - 0.7 % Show Supplier Material materials with Contracción of 0.6 - 0.7 % | ISO 294-4 | 60x60x2 mm, Transverse | |
Velocidad de flujo del volumen derretido | 14 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 14 cm³/10min | ISO 1133 | 220°C/10Kg |
Technological properties
| Property | ||
|---|---|---|
| Certifications | UL Certificate | |
| Color | White to slightly yellowish. | |
| Handling recommendations | Please see the Material Safety Data Sheet for relevant health & safety information. | |
| Other | Control measurements in other places may issue different results due to influences of machinery, equipment, test method or storage conditions. | |
| Processing methods | Injection molding-melt temperature: 240 ºC according to ISO 294 Injection molding-mold temperature: 70 ºC according to ISO 294 Injection molding-injection velocity: 240 mm/s according to ISO 294 | |