General
Property | Value | Testing Standard |
---|---|---|
Densidad | 1.05 g/cm³ Show Supplier Material materials with Densidad of 1.05 g/cm³ | ISO 1183-1 |
Mecánica
Property | Temperature | Value | Testing Standard | Comment |
---|---|---|---|---|
Elongación | 15 % Show Supplier Material materials with Elongación of 15 % | ISO 527-1/2 | min. | 50 mm/min | |
Elongation at yield | 2.5 % Show Supplier Material materials with Elongation at yield of 2.5 % | ISO 527-1/2 | 50 mm/min | |
Hardness, Ball Indentation | 105 MPa Show Supplier Material materials with Hardness, Ball Indentation of 105 MPa | ISO 2039-1 | ||
Límite elástico | 47 MPa Show Supplier Material materials with Límite elástico of 47 MPa | ISO 527-1/2 | 50 mm/min | |
Módulo de flexión | 2.4 GPa Show Supplier Material materials with Módulo de flexión of 2.4 GPa | ISO 527-1/2 | 2 mm/min | |
Módulo elástico | 2.4 GPa Show Supplier Material materials with Módulo elástico of 2.4 GPa | ISO 527-1/2 | 1 mm/min | |
Resistencia a la flexión | 72 MPa Show Supplier Material materials with Resistencia a la flexión of 72 MPa | ISO 178 | 2 mm/min | |
Resistencia al choque, ensayo Charpy entallado | -30 °C | 7 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 7 kJ/m² | ISO 179-1eA | |
23 °C | 17 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 17 kJ/m² | ISO 179-1eA | ||
Resistencia al choque, ensayo Charpy no entallado | -30 °C | 80 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 80 kJ/m² | ISO 179-1eU | |
23 °C | 90 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 90 kJ/m² | ISO 179-1eU |
Aplicaciones térmicas
Property | Value | Testing Standard | Pressure | Comment | |||
---|---|---|---|---|---|---|---|
Glow Wire Flammability Index | 700 °C Show Supplier Material materials with Glow Wire Flammability Index of 700 °C | IEC 60695-2-12 | 2.0 mm | ||||
Temperatura de flexión bajo carga | 98 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 98 °C | ISO 75-1/2 | 1.8 MPa | ||||
102 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 102 °C | ISO 75-1/2 | 0.45 MPa | |||||
Temperatura de reblandecimiento Vicat | 101 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 101 °C | ISO 306 | 50 N | 50°C/h | ||||
Inflamabilidad | At thickness 1.6 mm UL 94: HB. Burning rate US-FMVSS (2.0 mm): 60 mm/min according to ISO 3795 |
Eléctrico
Property | Value | Frequency | Testing Standard | Comment |
---|---|---|---|---|
Constante dieléctrica | 3 [-] Show Supplier Material materials with Constante dieléctrica of 3 [-] | 1MHz | IEC 60250 | |
3.1 [-] Show Supplier Material materials with Constante dieléctrica of 3.1 [-] | 100Hz | IEC 60250 | ||
Factor de disipación | 0.005 [-] Show Supplier Material materials with Factor de disipación of 0.005 [-] | 100Hz | IEC 60250 | |
0.008 [-] Show Supplier Material materials with Factor de disipación of 0.008 [-] | 1MHz | IEC 60250 | ||
Rigidez dieléctrica | 33 kV/mm Show Supplier Material materials with Rigidez dieléctrica of 33 kV/mm | IEC 60243-1 | 1 mm | |
Índice de seguimiento comparativo | 600 V Show Supplier Material materials with Índice de seguimiento comparativo of 600 V | IEC 60112 | Solution A |
Rheological Properties
Property | Value | Testing Standard | Comment |
---|---|---|---|
Contracción | 0.4 - 0.6 % Show Supplier Material materials with Contracción of 0.4 - 0.6 % | ISO 294-4 | 60x60x2 mm |
0.4 - 0.6 % Show Supplier Material materials with Contracción of 0.4 - 0.6 % | ISO 294-4 | 60x60x2 mm, Transverse | |
Velocidad de flujo del volumen derretido | 25 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 25 cm³/10min | ISO 1133 | 220°C/10Kg |
Technological properties
Property | ||
---|---|---|
Certifications | UL Certificate | |
Handling recommendations | Please see the Material Safety Data Sheet for relevant health & safety information. | |
Other | Control measurements in other places may issue different results due to influences of machinery, equipment, test method or storage conditions. | |
Processing methods | Injection molding-melt temperature: 240 ºC according to ISO 294 Injection molding-mold temperature: 70 ºC according to ISO 294 Injection molding-injection velocity: 240 mm/s according to ISO 294 |