Propiedades
General
| Property | Value |
|---|---|
Densidad | 1.45 g/cm³ Show Supplier Material materials with Densidad of 1.45 g/cm³ |
Mecánica
| Property | Value | Testing Standard |
|---|---|---|
Elongación | 17 % Show Supplier Material materials with Elongación of 17 % | DIN EN ISO 527-1 |
Módulo elástico | 2.5 GPa Show Supplier Material materials with Módulo elástico of 2.5 GPa | DIN EN ISO 527-1 |
Resistencia a la tracción | 42 MPa Show Supplier Material materials with Resistencia a la tracción of 42 MPa | DIN EN ISO 527-1 |
Resistencia al choque, ensayo Charpy no entallado | 80 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 80 kJ/m² | DIN EN ISO 179-1eU |
Aplicaciones térmicas
| Property | Value | Testing Standard | Comment | ||
|---|---|---|---|---|---|
Temperatura de fusión | 260 °C Show Supplier Material materials with Temperatura de fusión of 260 °C | DIN 53765 | |||
Temperatura de transición del vidrio | 72 °C Show Supplier Material materials with Temperatura de transición del vidrio of 72 °C | DIN 53765 | |||
Temperatura máx. de funcionamiento | 110 °C Show Supplier Material materials with Temperatura máx. de funcionamiento of 110 °C | Long | |||
170 °C Show Supplier Material materials with Temperatura máx. de funcionamiento of 170 °C | Short | ||||
Inflamabilidad | UL94 class HB, DIN IEC 60695-11-10 | ||||
Rheological Properties
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Velocidad de flujo de la masa derretida | 19 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 19 g/10min | DIN EN ISO 1133 | 280°C/2.16kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Food engineering | |
| Certifications | Explanation of food contact according to FDA and EU 10/2011 | |
| Color | Blue | |
| Detectability | Inductive: 6 mm Al, X-Ray detectable: 3.5 mm Al | |
| Fillers | Detectable Filler | |
| Processing methods | Permissible residual moisture content (%): 0.1, drying temperature (°C): 80, drying time (h): 8, mould temperature (°C): 150, material temperature (°C): 310, cylinder/processing temperature (°C): 310 | |