General
Property | Value |
---|---|
Densidad | 1.39 g/cm³ Show Supplier Material materials with Densidad of 1.39 g/cm³ |
Mecánica
Property | Value | Testing Standard |
---|---|---|
Elongación | 16 % Show Supplier Material materials with Elongación of 16 % | DIN EN ISO 527-1 |
Módulo elástico | 2.5 GPa Show Supplier Material materials with Módulo elástico of 2.5 GPa | DIN EN ISO 527-1 |
Resistencia a la tracción | 54 MPa Show Supplier Material materials with Resistencia a la tracción of 54 MPa | DIN EN ISO 527-1 |
Resistencia al choque, ensayo Charpy no entallado | 87 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 87 kJ/m² | DIN EN ISO 179-1eU |
Aplicaciones térmicas
Property | Value | Testing Standard | Pressure | Comment | |||
---|---|---|---|---|---|---|---|
Temperatura de flexión bajo carga | 215 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 215 °C | ISO-R 75 Method A | 1.8 MPa | ||||
Temperatura de fusión | 260 °C Show Supplier Material materials with Temperatura de fusión of 260 °C | ||||||
Temperatura de transición del vidrio | 72 °C Show Supplier Material materials with Temperatura de transición del vidrio of 72 °C | ||||||
Temperatura máx. de funcionamiento | 110 °C Show Supplier Material materials with Temperatura máx. de funcionamiento of 110 °C | Long | |||||
170 °C Show Supplier Material materials with Temperatura máx. de funcionamiento of 170 °C | Short | ||||||
Inflamabilidad | UL94 class HB for 0.8mm thickness, DIN IEC 60695-11-10 |
Rheological Properties
Property | Value | Testing Standard | Comment |
---|---|---|---|
Velocidad de flujo de la masa derretida | 28 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 28 g/10min | DIN EN ISO 1133 | 280°C/2.16kg |
Technological properties
Property | ||
---|---|---|
Certifications | Explanation of food contact according to FDA and EU 10/2011 on request | |
Color | Blue | |
Detectability | Inductive: 4.7 mm Al | |
Fillers | Detectable Filler | |
Processing methods | Permissible residual moisture content (%): 0.1, drying temperature (°C): 80, drying time (h): 8, mould temperature (°C): 150, material temperature (°C): 310, cylinder/processing temperature (°C): 310 |