General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.35 g/cm³ Show Supplier Material materials with Densidad of 1.35 g/cm³ | ISO 1183 |
Water content | 23.0 °C | 0.1 % Show Supplier Material materials with Water content of 0.1 % | ISO 15512 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 3 % Show Supplier Material materials with Elongación of 3 % | ISO 527-2 (5mm/min) |
Módulo de flexión | 23.0 °C | 9.2 GPa Show Supplier Material materials with Módulo de flexión of 9.2 GPa | ISO 178 (2mm/min) |
Módulo elástico | 23.0 °C | 11 GPa Show Supplier Material materials with Módulo elástico of 11 GPa | ISO 527-2 (1mm/min) |
Resistencia a la flexión | 23.0 °C | 300 MPa Show Supplier Material materials with Resistencia a la flexión of 300 MPa | ISO 178 (2mm/min) |
Resistencia a la tracción | 23.0 °C | 185 MPa Show Supplier Material materials with Resistencia a la tracción of 185 MPa | ISO 527-2 (5mm/min) |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 14 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 14 kJ/m² | ISO 179/1eA |
Resistencia al choque, ensayo Charpy no entallado | 23.0 °C | 90 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 90 kJ/m² | ISO 179/1eU |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 13 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 13 kJ/m² | ISO 180/1A |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 85 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod no entallado of 85 kJ/m² | ISO 180/1U |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Contenido de cenizas | 23.0 °C | 30 % Show Supplier Material materials with Contenido de cenizas of 30 % | ISO 3451-4 | ||
Heat deflection temperature, 0.45 MPa | 250 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 250 °C | ISO 75-2/B | |||
Heat deflection temperature, 1.80 MPa | 245 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 245 °C | ISO 75-2/A | |||
Temperatura de fusión | 260 °C Show Supplier Material materials with Temperatura de fusión of 260 °C | ISO 3146 | |||
Inflamabilidad | UL94 (0.8mm) HB |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Surface resistivity | 23.0 °C | 1.00E+14 Ω/sq Show Supplier Material materials with Surface resistivity of 1.00E+14 Ω/sq | ASTM D257 |
Índice de seguimiento comparativo | 23.0 °C | 400 V Show Supplier Material materials with Índice de seguimiento comparativo of 400 V | EN 60112 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Eplamid 66 GFH compounds are used in all sectors of industry especiallyautomotive under the hood applications, offering an excellent balance of thermal and mechanical properties. Its good for long term heat resistance as well as hyrdolysis resistant applications. | |
Fillers | 30% Glass Fiber | |
Other | Laboratory conditions are 23 ±2°C and 45-55 % RH. |