Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 0.94 g/cm³ Show Supplier Material materials with Densidad of 0.94 g/cm³ | ASTM D1505 |
Densidad aparente | 23.0 °C | 450 g/cm³ Show Supplier Material materials with Densidad aparente of 450 g/cm³ | ASTM D1525 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Dureza Shore D | 23.0 °C | 57 [-] Show Supplier Material materials with Dureza Shore D of 57 [-] | ASTM D2240 |
Elongación | 23.0 °C | 250 - 950 % Show Supplier Material materials with Elongación of 250 - 950 % | ASTM D638 |
Impact strength, Izod notched, ASTM | 23.0 °C | 500 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 500 J/m | ASTM D256, Partial Break |
Límite elástico | 23.0 °C | 19.75 - 20 MPa Show Supplier Material materials with Límite elástico of 19.75 - 20 MPa | ASTM D638 |
Módulo de flexión | 23.0 °C | 0.25 - 0.75 GPa Show Supplier Material materials with Módulo de flexión of 0.25 - 0.75 GPa | ASTM D790 |
Resistencia a la tracción | 23.0 °C | 12.25 MPa Show Supplier Material materials with Resistencia a la tracción of 12.25 MPa | ASTM D638 |
Aplicaciones térmicas
Property | Value | Comment |
---|---|---|
Temperatura de reblandecimiento Vicat | 118 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 118 °C | ASTM D1525 |
Rheological Properties
Property | Value | Comment |
---|---|---|
Velocidad de flujo de la masa derretida | 4 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 4 g/10min | ASTM D1238, 190°C/2.16kg |
Technological properties
Property | ||
---|---|---|
Application areas | Due to its combination of mechanical properties, ESCR resistance & fluidity, GREENETHENE G-3904U is suggested for the production of Playground equipment, manholes, storage containers, chemical & Oil tanks. | |
Certifications | List of Constituents of Polyethylene in Contact with Foodstuffs, Pharmaceuticals and Drinking Water: IS 10141:2001, IS 12701:1996 | |
Processing methods | Compression molded & rotomolded |