General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.02 g/cm³ Show Supplier Material materials with Densidad of 1.02 g/cm³ | ISO1183 |
Mecánica
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Dureza Shore D | 23.0 °C | 60 - 62 [-] Show Supplier Material materials with Dureza Shore D of 60 - 62 [-] | ISO868 | ||
Elongación | 23.0 °C | 300 % Show Supplier Material materials with Elongación of 300 % | ISO527 | ||
Límite elástico | 23.0 °C | 21 MPa Show Supplier Material materials with Límite elástico of 21 MPa | ISO527 | ||
Módulo de flexión | 23.0 °C | 0.3 GPa Show Supplier Material materials with Módulo de flexión of 0.3 GPa | ISO178 | ||
Resistencia a la flexión | 23.0 °C | 15 MPa Show Supplier Material materials with Resistencia a la flexión of 15 MPa | ISO178 | ||
Resistencia a la tracción | 23.0 °C | 48 MPa Show Supplier Material materials with Resistencia a la tracción of 48 MPa | ISO527 | ||
Resistencia al choque, ensayo Charpy entallado | -30.0 °C | 45 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 45 kJ/m² | ISO179 | ||
23.0 °C | 70 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 70 kJ/m² | ISO179 | |||
Resistencia al choque, ensayo Charpy no entallado | ISO179, No break @-30, 23°C |
Technological properties
Property | ||
---|---|---|
Application areas | Nylon badmintion, shuttlecock | |
Processing methods | Drying Temperature: 75-80°C, Drying Time: 3-4 hr, Rear Temperature: 180°C, Middle Temperature: 250°C, Front Temperature: 250°C, Nozzle Temperature: 230°C, Mold Temperature: 60-80°C, Injection Pressure: 70-100 MPa |