General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.32 g/cm³ Show Supplier Material materials with Densidad of 1.32 g/cm³ | ISO1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Dureza Shore D | 23.0 °C | 78 [-] Show Supplier Material materials with Dureza Shore D of 78 [-] | ISO868 |
Elongación | 23.0 °C | 7 % Show Supplier Material materials with Elongación of 7 % | ISO527 |
Módulo elástico | 23.0 °C | 8 GPa Show Supplier Material materials with Módulo elástico of 8 GPa | ISO527 |
Resistencia a la tracción | 23.0 °C | 130 MPa Show Supplier Material materials with Resistencia a la tracción of 130 MPa | ISO527 |
Resistencia al choque, ensayo Charpy entallado | -30.0 °C | 15 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 15 kJ/m² | ISO179 |
23.0 °C | 20 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 20 kJ/m² | ISO179 | |
Resistencia al choque, ensayo Charpy no entallado | -30.0 °C | 80 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 80 kJ/m² | ISO179 |
23.0 °C | 80 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 80 kJ/m² | ISO179 | |
Aplicaciones térmicas
Property | Value | Comment |
---|---|---|
Heat deflection temperature, 1.80 MPa | 160 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 160 °C | ISO75/A |
Technological properties
Property | ||
---|---|---|
Application areas | Tubing connection; Automotive lightweight components; Sport health equipment | |
Fillers | 40% Glass Fiber | |
Processing methods | Drying Temperature: 80-85°C, Drying Time: 3-4 hr, Rear Temperature: 190°C, Middle Temperature: 210°C, Front Temperature: 220°C, Nozzle Temperature: 210°C, Mold Temperature: 40-60°C, Injection Pressure: 80-100 MPa |