General
Property | Temperature | Value |
---|---|---|
Densidad | 23.0 °C | 8.9 g/cm³ Show Supplier Material materials with Densidad of 8.9 g/cm³ |
Medidas
Property | Value |
---|---|
Dimensions | Available size round products (mm): 1-35 |
Mecánica
Property | Temperature | Value |
---|---|---|
Dureza Brinell | 23.0 °C | 180 - 208 [-] Show Supplier Material materials with Dureza Brinell of 180 - 208 [-] |
Dureza Rockwell C | 23.0 °C | 10 - 17 [-] Show Supplier Material materials with Dureza Rockwell C of 10 - 17 [-] |
Dureza Vickers | 23.0 °C | 180 - 210 [-] Show Supplier Material materials with Dureza Vickers of 180 - 210 [-] |
Elongación | 23.0 °C | 1 % Show Supplier Material materials with Elongación of 1 % |
Límite elástico | 23.0 °C | 670 MPa Show Supplier Material materials with Límite elástico of 670 MPa |
Módulo elástico | 23.0 °C | 165 GPa Show Supplier Material materials with Módulo elástico of 165 GPa |
Resistencia a la tracción | 23.0 °C | 800 - 850 MPa Show Supplier Material materials with Resistencia a la tracción of 800 - 850 MPa |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 1.72E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.72E-5 1/K | for 20-200°C |
Conductividad térmica | 23.0 °C | 22.5 W/(m·K) Show Supplier Material materials with Conductividad térmica of 22.5 W/(m·K) | for 20-200°C |
Eléctrico
Property | Temperature | Value |
---|---|---|
Conductividad eléctrica | 23.0 °C | 2.00E+6 S/m Show Supplier Material materials with Conductividad eléctrica of 2.00E+6 S/m |
Magnético
Property | Temperature | Value |
---|---|---|
Permeabilidad magnética relativa | 23.0 °C | 1 [-] Show Supplier Material materials with Permeabilidad magnética relativa of 1 [-] |
Technological properties
Property | ||
---|---|---|
Application areas | Summary of typical applications: Mechanical parts in very demanding environments | |
Corrosion properties | Corrosion resistance rating: 5 out of 5 | |
General machinability | Machinability: 40 % | |
Processing history | Condition: H15 |