General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 0.92 g/cm³ Show Supplier Material materials with Densidad of 0.92 g/cm³ | ASTM D297 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Dureza Shore D | 23.0 °C | 48 - 50 [-] Show Supplier Material materials with Dureza Shore D of 48 - 50 [-] | ASTM 2240, for 5-15 seconds |
Elongación | 23.0 °C | 400 % Show Supplier Material materials with Elongación of 400 % | ASTM D412 |
Resistencia a desgarros | 23.0 °C | 90 kN/m Show Supplier Material materials with Resistencia a desgarros of 90 kN/m | ASTM D624 |
Resistencia a la tracción | 23.0 °C | 23 MPa Show Supplier Material materials with Resistencia a la tracción of 23 MPa | ASTM D412 |
Set de compresión | 23.0 °C | 49 [-] Show Supplier Material materials with Set de compresión of 49 [-] | ASTM D395, 22 h |
70.0 °C | 65 [-] Show Supplier Material materials with Set de compresión of 65 [-] | ASTM D395, 22 h | |
120.0 °C | 81 [-] Show Supplier Material materials with Set de compresión of 81 [-] | ASTM D395, 22 h | |
Aplicaciones térmicas
Property | Value | Comment |
---|---|---|
Brittleness temperature | -40 °C Show Supplier Material materials with Brittleness temperature of -40 °C | D746 |
Technological properties
Property | ||
---|---|---|
Processing methods | Extrusion: Hopper Temperature: 130-140°C, Middle Temperature: 140-160°C, Measurment Temperature: 160-180°C, Front Temperature: 170-190°C, Mold Temperature: 160-180°C, Melt Temperature: 150-170°C, Comp. Ratio:3:1, Screen: 20-60 Mesh - Injection: Rear Temperature: 130-150°C, Middle Temperature: 150-170°C, Front Temperature: 180-200°C, Nozzle Temperature: 180-190°C, Melt Temperature:160-190°C, Mold Temperature: 30-80°C, Speed: 100-200rpm, Back Pressure 0.07 - 0.7Mpa |