General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.02 - 0.04 % Show Material materials with Absorción de agua of 0.02 - 0.04 % | DIN EN ISO 62, 24h-96h |
Densidad | 23.0 °C | 1.16 g/cm³ Show Material materials with Densidad of 1.16 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.48 [-] Show Material materials with Coeficiente de Poisson of 0.48 [-] | |
Dureza Shore D | 23.0 °C | 60 [-] Show Material materials with Dureza Shore D of 60 [-] | max., ISO 7619-1 |
Elongación | 23.0 °C | 260 % Show Material materials with Elongación of 260 % | ISO 527-1,ISO 527-2 |
Hardness, Ball Indentation | 23.0 °C | 115 MPa Show Material materials with Hardness, Ball Indentation of 115 MPa | ISO 2039-1 |
Módulo de compresión | 23.0 °C | 2.8 MPa Show Material materials with Módulo de compresión of 2.8 MPa | EN ISO 604 |
Módulo de flexión | 23.0 °C | 0.27 GPa Show Material materials with Módulo de flexión of 0.27 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 0.27 GPa Show Material materials with Módulo elástico of 0.27 GPa | ISO 527-1, ISO 527-2 |
Resistencia a desgarros | 23.0 °C | 140 kN/m Show Material materials with Resistencia a desgarros of 140 kN/m | ISO 34-1 |
Resistencia a desgarros transversal | 23.0 °C | 130 kN/m Show Material materials with Resistencia a desgarros transversal of 130 kN/m | ISO 34-1 |
Resistencia a la compresión | 23.0 °C | 20 - 76 MPa Show Material materials with Resistencia a la compresión of 20 - 76 MPa | EN ISO 604, 1%-5% |
Resistencia a la tracción | 23.0 °C | 33 MPa Show Material materials with Resistencia a la tracción of 33 MPa | ISO 527-1,ISO 527-2 |
Resistencia al choque, ensayo Charpy entallado | -40.0 °C | 7 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 7 kJ/m² | ISO 179/1eA |
-30.0 °C | 12 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 12 kJ/m² | ISO 179/1eA | |
23.0 °C | 102 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 102 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | 23.0 °C | 37 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 37 kJ/m² | DIN EN ISO 179-1eU |
Resistencia al choque, ensayo Izod entallado | -40.0 °C | 7 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 7 kJ/m² | ISO 180/1A |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Brittleness temperature | -65 °C Show Material materials with Brittleness temperature of -65 °C | ISO 974 | |||
Coeficiente de dilatación térmica | 23.0 °C | 2E-4 1/K Show Material materials with Coeficiente de dilatación térmica of 2E-4 1/K | ISO 11359-1/2, for -40 to 23°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.8E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.8E-4 1/K | ISO 11359-1/2, for -40 to 23°C | ||
Heat deflection temperature, 0.45 MPa | 65 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 65 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 45 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 45 °C | ISO 75-1/-2 | |||
Temperatura de fusión | 215 °C Show Material materials with Temperatura de fusión of 215 °C | ISO 11357-1, ISO 11357-3, 18°F/min | |||
Temperatura de reblandecimiento Vicat | 60 - 195 °C Show Material materials with Temperatura de reblandecimiento Vicat of 60 - 195 °C | ISO 306, respectively for 90°F/h, 11lbf and 90°F/h, 2lbf | |||
Temperatura de transición del vidrio | 15 °C Show Material materials with Temperatura de transición del vidrio of 15 °C | ISO 11357-1, ISO 11357-2, 18°F/min | |||
Inflamabilidad | B ISO 3795 (FMVSS 302) | ||||
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 2.4 % Show Material materials with Contracción of 2.4 % | ISO 294-4, ISO 2577 |
Contracción transversal | 23.0 °C | 2.2 % Show Material materials with Contracción transversal of 2.2 % | ISO 294-4, ISO 2577 |
Velocidad de flujo de la masa derretida | 4 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 4 g/10min | ISO 1133, 240°C/10Kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Cable insulation and jacketing, Chassis suspension Systems, Food Contact Materials, Innovative Furniture Design, Mechanical Gears, Medical Device Materials, Mobile Phone Housing & Components, Plastics For Sporting Goods, Polymers for Oil and Gas, Railway Technology for the Long Haul, Seals and Gaskets, Sustainability in Airbag Systems, Thermoplastic Tubing and Elastomeric Hose | |
| Corrosion properties | In Acetic Acid, 5% loss by massa at 23°C | |
| Processing methods | Blow Molding, Drying Temperature: 80°C, Drying Time: 6-8hr, Processing Moisture Content: <0.03%, Melt Temperature: 235-250°C (Optimum:245°C), Swell Ratio: 1.6, Molding Temperature: 40-60°C (Optimum: 45) | |