General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 0.1 % Show Material materials with Absorción de agua of 0.1 % | ASTM D 570 | 24 Hours |
Densidad | 23.0 °C | 1.22 g/cm³ Show Material materials with Densidad of 1.22 g/cm³ | ASTM D 792 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongation at yield | 23.0 °C | 3.9 % Show Material materials with Elongation at yield of 3.9 % | ASTM D 638 | Type I, 50 mm/min |
Flexural yield strength | 23.0 °C | 56 MPa Show Material materials with Flexural yield strength of 56 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Impact strength, Izod notched, ASTM | -30.0 °C | 801 J/m Show Material materials with Impact strength, Izod notched, ASTM of 801 J/m | ASTM D 256 |
23.0 °C | 870 J/m Show Material materials with Impact strength, Izod notched, ASTM of 870 J/m | ASTM D 256 | |
Impact strength, Izod unnotched, ASTM | -30.0 °C | 3204 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 3204 J/m | ASTM D 4812 |
23.0 °C | 3204 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 3204 J/m | ASTM D 4812 | |
Límite elástico | 23.0 °C | 39 MPa Show Material materials with Límite elástico of 39 MPa | ASTM D 638 | Type I, 50 mm/min |
Módulo de flexión | 23.0 °C | 1.79 GPa Show Material materials with Módulo de flexión of 1.79 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Aplicaciones térmicas
Property | Value | Comment |
---|---|---|
Heat deflection temperature, 1.80 MPa | 47 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 47 °C | ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 2.4 - 2.7 % Show Material materials with Contracción of 2.4 - 2.7 % | SABIC method | 3.2 mm |
Contracción transversal | 23.0 °C | 2.4 - 2.7 % Show Material materials with Contracción transversal of 2.4 - 2.7 % | SABIC method |
Melt viscosity | 23.0 °C | 1200 Pa·s Show Material materials with Melt viscosity of 1200 Pa·s | SABIC method |
Velocidad de flujo de la masa derretida | 12.7 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 12.7 g/10min | ASTM D 1238 | 250°C/5.0 kgf |
Technological properties
Property | ||
---|---|---|
Application areas | Circuit Protection,LED lighting,Swimming Pool/Spa, underhood power distribution boxes and covers. | |
Processing methods | Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 12hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 245-260°C, Nozzle Temperature: 240-255°C, Front - Zone 3 Temperature: 245-260°C, Middle - Zone 2 Temperature: 240-255°C, Rear - Zone 1 Temperature: 230-250°C, Mold Temperature: 50-75°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 50-100rpm, Shot to Cylinder Size: 40-80%, Vent Depth: 0.013-0.025mm |