General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Densidad | 23.0 °C | 1.2 g/cm³ Show Material materials with Densidad of 1.2 g/cm³ | ASTM D 792 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 91 % Show Material materials with Elongación of 91 % | ASTM D 638 | Type I, 50 mm/min |
Elongation at yield | 23.0 °C | 7 % Show Material materials with Elongation at yield of 7 % | ASTM D 638 | Type I, 50 mm/min |
Flexural yield strength | 23.0 °C | 98 MPa Show Material materials with Flexural yield strength of 98 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Impact strength, Izod notched, ASTM | -30.0 °C | 112 J/m Show Material materials with Impact strength, Izod notched, ASTM of 112 J/m | ASTM D 256 |
23.0 °C | 826 J/m Show Material materials with Impact strength, Izod notched, ASTM of 826 J/m | ASTM D 256 | |
Límite elástico | 23.0 °C | 62 MPa Show Material materials with Límite elástico of 62 MPa | ASTM D 638 | Type I, 50 mm/min |
Módulo de flexión | 23.0 °C | 2.37 GPa Show Material materials with Módulo de flexión of 2.37 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Módulo elástico | 23.0 °C | 2.3 GPa Show Material materials with Módulo elástico of 2.3 GPa | ASTM D 638 | 50 mm/min |
Resistencia a la tracción | 23.0 °C | 60 MPa Show Material materials with Resistencia a la tracción of 60 MPa | ASTM D 638 | Type I, 50 mm/min |
Aplicaciones térmicas
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 6.6E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 6.6E-5 1/K | ASTM E 831 | -40°C to 40°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 6.7E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 6.7E-5 1/K | ASTM E 831 | -40°C to 40°C |
Heat deflection temperature, 1.80 MPa | 127 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 127 °C | ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed | |
Temperatura de reblandecimiento Vicat | 145 °C Show Material materials with Temperatura de reblandecimiento Vicat of 145 °C | ASTM D 1525 | Rate B/50 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.6 - 0.9 % Show Material materials with Contracción of 0.6 - 0.9 % | SABIC method | 3.2 mm |
Velocidad de flujo de la masa derretida | 3.2 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 3.2 g/10min | ASTM D 1238 | 300°C/1.2 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | LED Lighting | |
| Processing methods | Drying Temperature: 75-90°C, Drying Time: 2-4hrs, Minimum Moisture Content: 0.04%, Melt Temperature: 180-200°C, Barrel - Zone 1 Temperature: 165°C, Barrel - Zone 2 Temperature: 170°C, Barrel - Zone 3 Temperature: 175°C, Barrel - Zone 4 Temperature: 180°C, Roll Stack Temperature - Top: 175-180°C, Roll Stack Temperature - Middle: 175-180°C, Roll Stack Temperature - Bottom: 175-180°C | |