General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 0.9 % Show Material materials with Absorción de agua of 0.9 % | Sim. to ISO 62 | 80mil |
Densidad | 23.0 °C | 1.42 g/cm³ Show Material materials with Densidad of 1.42 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.37 [-] Show Material materials with Coeficiente de Poisson of 0.37 [-] | |
Elongación | 23.0 °C | 25 % Show Material materials with Elongación of 25 % | ISO 527-1/-2 |
Elongation at yield | 23.0 °C | 12 % Show Material materials with Elongation at yield of 12 % | ISO 527-1/-2 |
Límite elástico | 23.0 °C | 73 MPa Show Material materials with Límite elástico of 73 MPa | ISO 527-1/-2 |
Módulo de flexión | 23.0 °C | 3.2 GPa Show Material materials with Módulo de flexión of 3.2 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 3.4 GPa Show Material materials with Módulo elástico of 3.4 GPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -6.0 °C | 6 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 6 kJ/m² | ISO 179/1eA |
23.0 °C | 7 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 7 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | -6.0 °C | 200 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 200 kJ/m² | ISO 179/1eU |
23.0 °C | 220 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 220 kJ/m² | ISO 179/1eU | |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 1E-4 1/K Show Material materials with Coeficiente de dilatación térmica of 1E-4 1/K | ISO 11359-1/-2 |
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.1E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.1E-4 1/K | ISO 11359-1/-2 |
Heat deflection temperature, 0.45 MPa | 163 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 163 °C | ISO 75-1/-2 | |
Heat deflection temperature, 1.80 MPa | 107 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 107 °C | ISO 75-1/-2 | |
Temperatura de fusión | 178 °C Show Material materials with Temperatura de fusión of 178 °C | ISO 11357-1/-3 | 18°F/min | |
Temperatura de reblandecimiento Vicat | 160 °C Show Material materials with Temperatura de reblandecimiento Vicat of 160 °C | ISO 306 | 90°F/h, 11 lbf |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 1.9 % Show Material materials with Contracción of 1.9 % | ISO 294-4, 2577 |
Contracción transversal | 23.0 °C | 1.8 % Show Material materials with Contracción transversal of 1.8 % | ISO 294-4, 2577 |
Velocidad de flujo del volumen derretido | 13 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 13 cm³/10min | ISO 1133 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 215°C, Min. melt temperature: 210°C, Max. melt temperature: 220°C, Mold Temperature Optimum: 90°C, Min. mold temperature: 80°C, Max. mold temperature: 100°C, Hold pressure range: 80-100MPa, Hold pressure time: 7.5s/mm |