General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.16 g/cm³ Show Material materials with Densidad of 1.16 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Dureza Shore D | 23.0 °C | 49 [-] Show Material materials with Dureza Shore D of 49 [-] | max., ISO 7619-1 |
Elongación | 23.0 °C | 600 % Show Material materials with Elongación of 600 % | ISO 527-1/-2 |
Módulo de flexión | 23.0 °C | 0.35 GPa Show Material materials with Módulo de flexión of 0.35 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 0.29 GPa Show Material materials with Módulo elástico of 0.29 GPa | ISO 527-1/-2 |
Resistencia a desgarros | 23.0 °C | 110 kN/m Show Material materials with Resistencia a desgarros of 110 kN/m | ISO 34-1 |
Resistencia a desgarros transversal | 23.0 °C | 90 kN/m Show Material materials with Resistencia a desgarros transversal of 90 kN/m | ISO 34-1 |
Resistencia a la tracción | 23.0 °C | 30 MPa Show Material materials with Resistencia a la tracción of 30 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -40.0 °C | 120 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 120 kJ/m² | ISO 179/1eA |
-6.0 °C | 110 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 110 kJ/m² | ISO 179/1eA | |
Aplicaciones térmicas
Property | Value | Comment | |
---|---|---|---|
Brittleness temperature | -100 °C Show Material materials with Brittleness temperature of -100 °C | ISO 974 | |
Heat deflection temperature, 0.45 MPa | 48 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 48 °C | ISO 75-1/-2 | |
Heat deflection temperature, 1.80 MPa | 41 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 41 °C | ISO 75-1/-2 | |
Temperatura de fusión | 222 °C Show Material materials with Temperatura de fusión of 222 °C | ISO 11357-1/-3 | 18°F/min | |
Temperatura de reblandecimiento Vicat | 150 °C Show Material materials with Temperatura de reblandecimiento Vicat of 150 °C | ISO 306 | 90°F, 2 lbf | |
Inflamabilidad | FMVSS Class: B -, Burning rate, Thickness 1 mm: 24 mm/min |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 1.2 % Show Material materials with Contracción of 1.2 % | ISO 294-4, 2577 |
Contracción transversal | 23.0 °C | 1.2 % Show Material materials with Contracción transversal of 1.2 % | ISO 294-4, 2577 |
Velocidad de flujo de la masa derretida | 13 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 13 g/10min | ISO 1133 | 240°C/2.16kg | |
Velocidad de flujo del volumen derretido | 13 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 13 cm³/10min | ISO 1133 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 3-4h, Processing Moisture Content: ≤0.05%, Melt Temperature Optimum: 245°C, Min. melt temperature: 240°C, Max. melt temperature: 250°C, Mold Temperature Optimum: 45°C, Min. mold temperature: 40°C, Max. mold temperature: 55°C |