General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 0.6 % Show Material materials with Absorción de agua of 0.6 % | Sim. to ISO 62 | 80mil |
Densidad | 23.0 °C | 1.23 g/cm³ Show Material materials with Densidad of 1.23 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.48 [-] Show Material materials with Coeficiente de Poisson of 0.48 [-] | |||
Dureza Shore D | 23.0 °C | 66 [-] Show Material materials with Dureza Shore D of 66 [-] | max., ISO 7619-1 | ||
Elongación | 23.0 °C | 380 % Show Material materials with Elongación of 380 % | ISO 527-1/-2 | ||
Elongation at yield | 23.0 °C | 29 % Show Material materials with Elongation at yield of 29 % | ISO 527-1/-2 | ||
Límite elástico | 23.0 °C | 20 MPa Show Material materials with Límite elástico of 20 MPa | ISO 527-1/-2 | ||
Módulo elástico | 23.0 °C | 0.31 GPa Show Material materials with Módulo elástico of 0.31 GPa | ISO 527-1/-2 | ||
Resistencia a la tracción | 23.0 °C | 35 MPa Show Material materials with Resistencia a la tracción of 35 MPa | ISO 527-1/-2 | ||
Resistencia al choque, ensayo Charpy entallado | -6.0 °C | 13 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 13 kJ/m² | ISO 179/1eA | ||
23.0 °C | 110 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 110 kJ/m² | ISO 179/1eA | |||
Resistencia al choque, ensayo Charpy no entallado | No Break @ 23°C, ISO 179/1eU |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Calor específico | 23.0 °C | 2150 J/(kg·K) Show Material materials with Calor específico of 2150 J/(kg·K) | of melt | ||
Difusividad térmica | 23.0 °C | 0 mm²/s Show Material materials with Difusividad térmica of 0 mm²/s | |||
Heat deflection temperature, 0.45 MPa | 87 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 87 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 45 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 45 °C | ISO 75-1/-2 | |||
Temperatura de fusión | 211 °C Show Material materials with Temperatura de fusión of 211 °C | ISO 11357-1/-3 | 18°F/min | |||
Temperatura de reblandecimiento Vicat | 100 °C Show Material materials with Temperatura de reblandecimiento Vicat of 100 °C | ISO 306 | 90°F/h, 11 lbf | |||
Temperatura de transición del vidrio | 0 °C Show Material materials with Temperatura de transición del vidrio of 0 °C | ISO 11357-1/-2 | 18°F/min | |||
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, Burning Behav. at thickness h: HB class, Thickness tested: 3 mm, Oxygen index: 21 %, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 1.4 % Show Material materials with Contracción of 1.4 % | ISO 294-4, 2577 |
Contracción transversal | 23.0 °C | 1.4 % Show Material materials with Contracción transversal of 1.4 % | ISO 294-4, 2577 |
Velocidad de flujo de la masa derretida | 13 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 13 g/10min | ISO 1133 | 240°C/2.16kg |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 110°C, Drying Time, Dehumidified Dryer: 2-3h, Processing Moisture Content: ≤0.08%, Melt Temperature Optimum: 245°C, Min. melt temperature: 240°C, Max. melt temperature: 260°C, Mold Temperature Optimum: 45°C, Min. mold temperature: 45°C, Max. mold temperature: 55°C, Hold pressure range: ≤70MPa |