Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.45 [-] Show Material materials with Coeficiente de Poisson of 0.45 [-] | |
Dureza Shore D | 23.0 °C | 71 [-] Show Material materials with Dureza Shore D of 71 [-] | max., ISO 7619-1 |
Elongación | 23.0 °C | 250 % Show Material materials with Elongación of 250 % | ISO 527-1/-2 |
Elongation at yield | 23.0 °C | 19 % Show Material materials with Elongation at yield of 19 % | ISO 527-1/-2 |
Límite elástico | 23.0 °C | 38 MPa Show Material materials with Límite elástico of 38 MPa | ISO 527-1/-2 |
Módulo de flexión | 23.0 °C | 1.04 GPa Show Material materials with Módulo de flexión of 1.04 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 1.05 GPa Show Material materials with Módulo elástico of 1.05 GPa | ISO 527-1/-2 |
Resistencia a la tracción | 23.0 °C | 49 MPa Show Material materials with Resistencia a la tracción of 49 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -40.0 °C | 3.5 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 3.5 kJ/m² | ISO 179/1eA |
23.0 °C | 5.5 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 5.5 kJ/m² | ISO 179/1eA | |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 110°C, Drying Time, Dehumidified Dryer: 2-3h, Processing Moisture Content: ≤0.08%, Melt Temperature Optimum: 250°C, Min. melt temperature: 245°C, Max. melt temperature: 260°C, Mold Temperature Optimum: 45°C, Min. mold temperature: 45°C, Max. mold temperature: 55°C, Hold pressure range: ≥70MPa |