Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.25 g/cm³ Show Material materials with Densidad of 1.25 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.47 [-] Show Material materials with Coeficiente de Poisson of 0.47 [-] | |
Dureza Shore D | 23.0 °C | 71 [-] Show Material materials with Dureza Shore D of 71 [-] | max., ISO 7619-1 |
Elongación | 23.0 °C | 590 % Show Material materials with Elongación of 590 % | ISO 527-1/-2 |
Módulo de flexión | 23.0 °C | 0.51 GPa Show Material materials with Módulo de flexión of 0.51 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 0.51 GPa Show Material materials with Módulo elástico of 0.51 GPa | ISO 527-1/-2 |
Resistencia a desgarros | 23.0 °C | 180 kN/m Show Material materials with Resistencia a desgarros of 180 kN/m | ISO 34-1 |
Resistencia a desgarros transversal | 23.0 °C | 165 kN/m Show Material materials with Resistencia a desgarros transversal of 165 kN/m | ISO 34-1 |
Resistencia a la tracción | 23.0 °C | 50 MPa Show Material materials with Resistencia a la tracción of 50 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -40.0 °C | 5 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 5 kJ/m² | ISO 179/1eA |
Aplicaciones térmicas
Property | Value | Comment | |
---|---|---|---|
Brittleness temperature | -68 °C Show Material materials with Brittleness temperature of -68 °C | ISO 974 | |
Temperatura de fusión | 216 °C Show Material materials with Temperatura de fusión of 216 °C | ISO 11357-1/-3 | 18°F/min | |
Temperatura de reblandecimiento Vicat | 204 °C Show Material materials with Temperatura de reblandecimiento Vicat of 204 °C | ISO 306 | 90°F, 2 lbf | |
Inflamabilidad | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 110°C, Drying Time, Dehumidified Dryer: 2-3h, Processing Moisture Content: ≤0.08%, Melt Temperature Optimum: 245°C, Min. melt temperature: 235°C, Max. melt temperature: 260°C, Mold Temperature Optimum: 45°C, Min. mold temperature: 45°C, Max. mold temperature: 55°C, Hold pressure range: ≤70MPa |