General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.18 g/cm³ Show Material materials with Densidad of 1.18 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Dureza Shore D | 23.0 °C | 40 [-] Show Material materials with Dureza Shore D of 40 [-] | max., ISO 7619-1 | ||
Elongación | 23.0 °C | 360 % Show Material materials with Elongación of 360 % | ISO 527-1/-2 | ||
Módulo de cizallamiento | 23.0 °C | 0.02 GPa Show Material materials with Módulo de cizallamiento of 0.02 GPa | ISO 6721 | ||
Módulo de flexión | 23.0 °C | 0.07 GPa Show Material materials with Módulo de flexión of 0.07 GPa | ISO 178 | ||
Módulo elástico | 23.0 °C | 0.06 GPa Show Material materials with Módulo elástico of 0.06 GPa | ISO 527-1/-2 | ||
Resistencia a desgarros | 23.0 °C | 86 kN/m Show Material materials with Resistencia a desgarros of 86 kN/m | ISO 34-1 | ||
Resistencia a desgarros transversal | 23.0 °C | 96 kN/m Show Material materials with Resistencia a desgarros transversal of 96 kN/m | ISO 34-1 | ||
Resistencia a la tracción | 23.0 °C | 20 MPa Show Material materials with Resistencia a la tracción of 20 MPa | ISO 527-1/-2 | ||
Resistencia al choque, ensayo Charpy entallado | No Break @ 23,-6°C, ISO 179/1eA | ||||
Resistencia al choque, ensayo Charpy no entallado | No Break @ 23,-6°C, ISO 179/1eA | ||||
Resistencia al choque, ensayo Izod no entallado | No Break @ 23,-40°C, ISO180/1A |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Brittleness temperature | -60 °C Show Material materials with Brittleness temperature of -60 °C | ISO 974 | |||
Calor específico | 23.0 °C | 2050 J/(kg·K) Show Material materials with Calor específico of 2050 J/(kg·K) | of melt | ||
Coeficiente de dilatación térmica | 23.0 °C | 2.2E-4 1/K Show Material materials with Coeficiente de dilatación térmica of 2.2E-4 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.8E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.8E-4 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Difusividad térmica | 23.0 °C | 0 mm²/s Show Material materials with Difusividad térmica of 0 mm²/s | |||
Relative temperature index, electrical | 90 °C Show Material materials with Relative temperature index, electrical of 90 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 85 °C Show Material materials with Relative temperature index, mechanical impact of 85 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 85 °C Show Material materials with Relative temperature index, mechanical strength of 85 °C | UL 746B | 120mil | |||
Temperatura de fusión | 170 °C Show Material materials with Temperatura de fusión of 170 °C | ISO 11357-1/-3 | 18°F/min | |||
Temperatura de reblandecimiento Vicat | 115 °C Show Material materials with Temperatura de reblandecimiento Vicat of 115 °C | ISO 306 | 90°F, 2 lbf | |||
Temperatura de transición del vidrio | -35 °C Show Material materials with Temperatura de transición del vidrio of -35 °C | ISO 11357-1/-2 | 18°F/min | |||
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 3 mm, UL recognition: yes -, Oxygen index: 20 %, FMVSS Class: B -, Burning rate, Thickness 1 mm: 51 mm/min |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Constante dieléctrica, 1 MHz | 23.0 °C | 5 [-] Show Material materials with Constante dieléctrica, 1 MHz of 5 [-] | IEC 62631-2-1 |
Constante dieléctrica, 100 Hz | 23.0 °C | 5.7 [-] Show Material materials with Constante dieléctrica, 100 Hz of 5.7 [-] | IEC 62631-2-1 |
Dissipation factor, 100Hz | 23.0 °C | 0.06 [-] Show Material materials with Dissipation factor, 100Hz of 0.06 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.05 [-] Show Material materials with Dissipation factor, 1MHz of 0.05 [-] | IEC 62631-2-1 |
Rigidez dieléctrica | 23.0 °C | 17 kV/mm Show Material materials with Rigidez dieléctrica of 17 kV/mm | IEC 60243-1 |
Surface resistivity | 23.0 °C | 2.00E+13 Ω/sq Show Material materials with Surface resistivity of 2.00E+13 Ω/sq | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 4.00E+11 Ω·cm Show Material materials with Volume resistivity of 4.00E+11 Ω·cm | IEC 62631-3-1 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.8 % Show Material materials with Contracción of 0.8 % | ISO 294-4, 2577 |
Contracción transversal | 23.0 °C | 0.8 % Show Material materials with Contracción transversal of 0.8 % | ISO 294-4, 2577 |
Velocidad de flujo de la masa derretida | 5.3 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 5.3 g/10min | ISO 1133 | 190°C/2.16kg | |
Velocidad de flujo del volumen derretido | 5 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 5 cm³/10min | ISO 1133 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 2-3h, Processing Moisture Content: ≤0.08%, Melt Temperature Optimum: 200°C, Min. melt temperature: 190°C, Max. melt temperature: 220°C, Mold Temperature Optimum: 40°C, Min. mold temperature: 30°C, Max. mold temperature: 40°C |