Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 0.7 % Show Material materials with Absorción de agua of 0.7 % | Sim. to ISO 62 | 80mil |
Densidad | 23.0 °C | 1.16 g/cm³ Show Material materials with Densidad of 1.16 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.5 [-] Show Material materials with Coeficiente de Poisson of 0.5 [-] | |||
Dureza Shore D | 23.0 °C | 38 [-] Show Material materials with Dureza Shore D of 38 [-] | ISO 7619-1 | 15 seconds | ||
Elongación | 23.0 °C | 300 % Show Material materials with Elongación of 300 % | min. | ISO 527-1/-2 | ||
Módulo elástico | 23.0 °C | 0.06 GPa Show Material materials with Módulo elástico of 0.06 GPa | ISO 527-1/-2 | ||
Resistencia a desgarros | 23.0 °C | 110 kN/m Show Material materials with Resistencia a desgarros of 110 kN/m | ISO 34-1 | ||
Resistencia a la tracción | 23.0 °C | 26 MPa Show Material materials with Resistencia a la tracción of 26 MPa | ISO 527-1/-2 | ||
Resistencia al choque, ensayo Charpy entallado | No Break @ 23,-6,-40°C, ISO 179/1eA | ||||
Resistencia al choque, ensayo Charpy no entallado | No Break @ 23,-6°C, ISO 179/1eA |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 2.2E-4 1/K Show Material materials with Coeficiente de dilatación térmica of 2.2E-4 1/K | ISO 11359-1/-2 | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 2.2E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 2.2E-4 1/K | ISO 11359-1/-2 | ||
Difusividad térmica | 23.0 °C | 0 mm²/s Show Material materials with Difusividad térmica of 0 mm²/s | |||
Heat deflection temperature, 0.45 MPa | 50 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 50 °C | ISO 75-1/-2 | |||
Temperatura de fusión | 150 °C Show Material materials with Temperatura de fusión of 150 °C | ISO 11357-1/-3 | 18°F/min | |||
Temperatura de transición del vidrio | -50 °C Show Material materials with Temperatura de transición del vidrio of -50 °C | ISO 11357-1/-2 | 18°F/min | |||
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Oxygen index: 20 %, FMVSS Class: SE - |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Constante dieléctrica, 1 MHz | 23.0 °C | 4.7 [-] Show Material materials with Constante dieléctrica, 1 MHz of 4.7 [-] | IEC 62631-2-1 |
Constante dieléctrica, 100 Hz | 23.0 °C | 5.2 [-] Show Material materials with Constante dieléctrica, 100 Hz of 5.2 [-] | IEC 62631-2-1 |
Dissipation factor, 100Hz | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor, 100Hz of 0.01 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.05 [-] Show Material materials with Dissipation factor, 1MHz of 0.05 [-] | IEC 62631-2-1 |
Rigidez dieléctrica | 23.0 °C | 18 kV/mm Show Material materials with Rigidez dieléctrica of 18 kV/mm | IEC 60243-1 |
Surface resistivity | 23.0 °C | 2.00E+14 Ω/sq Show Material materials with Surface resistivity of 2.00E+14 Ω/sq | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 7.00E+12 Ω·cm Show Material materials with Volume resistivity of 7.00E+12 Ω·cm | IEC 62631-3-1 |
Índice de seguimiento comparativo | 23.0 °C | 600 V Show Material materials with Índice de seguimiento comparativo of 600 V | IEC 60112 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.2 % Show Material materials with Contracción of 0.2 % | ISO 294-4, 2577 |
Contracción transversal | 23.0 °C | 0.4 % Show Material materials with Contracción transversal of 0.4 % | ISO 294-4, 2577 |
Velocidad de flujo de la masa derretida | 5.3 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 5.3 g/10min | ISO 1133 | 190°C/2.16kg | |
Velocidad de flujo del volumen derretido | 5 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 5 cm³/10min | ISO 1133 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-3h, Processing Moisture Content: ≤0.08%, Melt Temperature Optimum: 180°C, Min. melt temperature: 170°C, Max. melt temperature: 190°C, Mold Temperature Optimum: 40°C, Min. mold temperature: 30°C, Max. mold temperature: 40°C |