General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.5 % Show Material materials with Absorción de agua of 0.5 % | Sim. to ISO 62 | 80mil |
Coefficient of friction | 0.2 [-] Show Material materials with Coefficient of friction of 0.2 [-] | ASTM 1894 | against steel | |
Densidad | 23.0 °C | 1.14 g/cm³ Show Material materials with Densidad of 1.14 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.49 [-] Show Material materials with Coeficiente de Poisson of 0.49 [-] | |||
Dureza Shore D | 23.0 °C | 40 [-] Show Material materials with Dureza Shore D of 40 [-] | max., ISO 7619-1 | ||
Elongación | 23.0 °C | 350 % Show Material materials with Elongación of 350 % | ISO 527-1/-2 | ||
Módulo de flexión | 23.0 °C | 0.08 GPa Show Material materials with Módulo de flexión of 0.08 GPa | ISO 178 | ||
Módulo elástico | 23.0 °C | 0.08 GPa Show Material materials with Módulo elástico of 0.08 GPa | ISO 527-1/-2 | ||
Resistencia a desgarros | 23.0 °C | 110 kN/m Show Material materials with Resistencia a desgarros of 110 kN/m | ISO 34-1 | ||
Resistencia a desgarros transversal | 23.0 °C | 115 kN/m Show Material materials with Resistencia a desgarros transversal of 115 kN/m | ISO 34-1 | ||
Resistencia a la tracción | 23.0 °C | 28 MPa Show Material materials with Resistencia a la tracción of 28 MPa | ISO 527-1/-2 | ||
Resistencia al choque, ensayo Charpy entallado | No Break @ 23,-40°C, ISO179/1A | ||||
Resistencia al choque, ensayo Charpy no entallado | No Break @ 23,-6°C, ISO 179/1eA | ||||
Resistencia al choque, ensayo Izod no entallado | No Break @ 23°C, ISO 179/1eU | ||||
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Brittleness temperature | -100 °C Show Material materials with Brittleness temperature of -100 °C | ISO 974 | |||
Calor específico | 23.0 °C | 2100 J/(kg·K) Show Material materials with Calor específico of 2100 J/(kg·K) | of melt | ||
Coeficiente de dilatación térmica | 23.0 °C | 2.3E-4 1/K Show Material materials with Coeficiente de dilatación térmica of 2.3E-4 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 2.4E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 2.4E-4 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Difusividad térmica | 23.0 °C | 0 mm²/s Show Material materials with Difusividad térmica of 0 mm²/s | |||
Heat deflection temperature, 0.45 MPa | 56 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 56 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 42 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 42 °C | ISO 75-1/-2 | |||
Temperatura de fusión | 207 °C Show Material materials with Temperatura de fusión of 207 °C | ISO 11357-1/-3 | 18°F/min | |||
Temperatura de reblandecimiento Vicat | 158 °C Show Material materials with Temperatura de reblandecimiento Vicat of 158 °C | ISO 306 | 90°F, 2 lbf | |||
Temperatura de transición del vidrio | -40 °C Show Material materials with Temperatura de transición del vidrio of -40 °C | ISO 11357-1/-2 | 18°F/min | |||
Inflamabilidad | FMVSS Class: B -, Burning rate, Thickness 1 mm: 17 mm/min | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dissipation factor, 100Hz | 23.0 °C | 0.03 [-] Show Material materials with Dissipation factor, 100Hz of 0.03 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 9.5E-3 [-] Show Material materials with Dissipation factor, 1MHz of 9.5E-3 [-] | IEC 62631-2-1 |
Rigidez dieléctrica | 23.0 °C | 19 kV/mm Show Material materials with Rigidez dieléctrica of 19 kV/mm | IEC 60243-1 |
Surface resistivity | 23.0 °C | 4.00E+14 Ω/sq Show Material materials with Surface resistivity of 4.00E+14 Ω/sq | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 8.00E+12 Ω·cm Show Material materials with Volume resistivity of 8.00E+12 Ω·cm | IEC 62631-3-1 |
Índice de seguimiento comparativo | 23.0 °C | 600 V Show Material materials with Índice de seguimiento comparativo of 600 V | IEC 60112 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 1.6 % Show Material materials with Contracción of 1.6 % | ISO 294-4, 2577 |
Contracción transversal | 23.0 °C | 1.5 % Show Material materials with Contracción transversal of 1.5 % | ISO 294-4, 2577 |
Velocidad de flujo de la masa derretida | 0.9 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 0.9 g/10min | ISO 1133 | 230°C/2.16kg |
Technological properties
| Property | ||
|---|---|---|
| Fillers | Carbon Black | |
| Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 3-4h, Processing Moisture Content: ≤0.08%, Melt Temperature Optimum: 240°C, Min. melt temperature: 230°C, Max. melt temperature: 250°C, Mold Temperature Optimum: 45°C, Min. mold temperature: 40°C, Max. mold temperature: 50°C, Ejection temperature: 145°C | |