Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.16 g/cm³ Show Material materials with Densidad of 1.16 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Dureza Shore D | 23.0 °C | 42 [-] Show Material materials with Dureza Shore D of 42 [-] | ISO 7619-1 | 15 seconds | ||
Elongación | 23.0 °C | 300 % Show Material materials with Elongación of 300 % | min. | ISO 527-1/-2 | ||
Módulo de flexión | 23.0 °C | 0.12 GPa Show Material materials with Módulo de flexión of 0.12 GPa | ISO 178 | ||
Módulo elástico | 23.0 °C | 0.11 GPa Show Material materials with Módulo elástico of 0.11 GPa | ISO 527-1/-2 | ||
Resistencia a desgarros | 23.0 °C | 110 kN/m Show Material materials with Resistencia a desgarros of 110 kN/m | ISO 34-1 | ||
Resistencia a desgarros transversal | 23.0 °C | 95 kN/m Show Material materials with Resistencia a desgarros transversal of 95 kN/m | ISO 34-1 | ||
Resistencia a la tracción | 23.0 °C | 33 MPa Show Material materials with Resistencia a la tracción of 33 MPa | ISO 527-1/-2 | ||
Resistencia al choque, ensayo Charpy entallado | No Break @ -40°C, ISO 179/1eA |
Aplicaciones térmicas
Property | Value | Comment | |
---|---|---|---|
Temperatura de fusión | 207 °C Show Material materials with Temperatura de fusión of 207 °C | ISO 11357-1/-3 | 18°F/min | |
Temperatura de reblandecimiento Vicat | 157 °C Show Material materials with Temperatura de reblandecimiento Vicat of 157 °C | ISO 306 | 90°F, 2 lbf | |
Inflamabilidad | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Rheological Properties
Property | Value | Comment |
---|---|---|
Velocidad de flujo de la masa derretida | 1.2 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 1.2 g/10min | ISO 1133 | 230°C/2.16kg |
Technological properties
Property | ||
---|---|---|
Fillers | Carbon Black | |
Processing methods | Drying Recommended: yes, Drying Temperature: 110°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.08%, Melt Temperature Optimum: 235°C, Min. melt temperature: 220°C, Max. melt temperature: 250°C, Mold Temperature Optimum: 45°C, Min. mold temperature: 40°C, Max. mold temperature: 50°C |