General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 1.9 % Show Material materials with Absorción de agua of 1.9 % | Sim. to ISO 62 | Immersion 24h |
Densidad | 23.0 °C | 1.43 g/cm³ Show Material materials with Densidad of 1.43 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Dureza Shore D | 23.0 °C | 44 [-] Show Material materials with Dureza Shore D of 44 [-] | max., ISO 7619-1 |
Elongación | 23.0 °C | 340 % Show Material materials with Elongación of 340 % | ISO 527-1/-2 |
Módulo de flexión | 23.0 °C | 0.15 GPa Show Material materials with Módulo de flexión of 0.15 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 0.14 GPa Show Material materials with Módulo elástico of 0.14 GPa | ISO 527-1/-2 |
Resistencia a desgarros | 23.0 °C | 70 kN/m Show Material materials with Resistencia a desgarros of 70 kN/m | ISO 34-1 |
Resistencia a desgarros transversal | 23.0 °C | 70 kN/m Show Material materials with Resistencia a desgarros transversal of 70 kN/m | ISO 34-1 |
Resistencia a la tracción | 23.0 °C | 13 MPa Show Material materials with Resistencia a la tracción of 13 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -40.0 °C | 5 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 5 kJ/m² | ISO 179/1eA |
-6.0 °C | 7 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 7 kJ/m² | ISO 179/1eA | |
23.0 °C | 40 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 40 kJ/m² | ISO 179/1eA | |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Brittleness temperature | -48 °C Show Material materials with Brittleness temperature of -48 °C | ISO 974 | |||
Coeficiente de dilatación térmica | 23.0 °C | 1.5E-4 1/K Show Material materials with Coeficiente de dilatación térmica of 1.5E-4 1/K | ISO 11359-1/-2 | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.7E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.7E-4 1/K | ISO 11359-1/-2 | ||
Difusividad térmica | 23.0 °C | 0 mm²/s Show Material materials with Difusividad térmica of 0 mm²/s | |||
Heat deflection temperature, 0.45 MPa | 46 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 46 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 41 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 41 °C | ISO 75-1/-2 | |||
Relative temperature index, electrical | 50 °C Show Material materials with Relative temperature index, electrical of 50 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 50 °C Show Material materials with Relative temperature index, mechanical impact of 50 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 50 °C Show Material materials with Relative temperature index, mechanical strength of 50 °C | UL 746B | 120mil | |||
Temperatura de fusión | 170 °C Show Material materials with Temperatura de fusión of 170 °C | ISO 11357-1/-3 | 18°F/min | |||
Temperatura de reblandecimiento Vicat | 107 °C Show Material materials with Temperatura de reblandecimiento Vicat of 107 °C | ISO 306 | 90°F, 2 lbf | |||
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: V-0 class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: V-0 class, Thickness tested: 3 mm, UL recognition: yes -, Oxygen index: 26 %, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Eléctrico
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 1.1 % Show Material materials with Contracción of 1.1 % | ISO 294-4, 2577 |
Contracción transversal | 23.0 °C | 1.1 % Show Material materials with Contracción transversal of 1.1 % | ISO 294-4, 2577 |
Velocidad de flujo de la masa derretida | 4 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 4 g/10min | ISO 1133 | 190°C/2.16kg | |
Velocidad de flujo del volumen derretido | 3.6 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 3.6 cm³/10min | ISO 1133 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 2-3h, Processing Moisture Content: ≤0.08%, Melt Temperature Optimum: 200°C, Min. melt temperature: 190°C, Max. melt temperature: 210°C, Mold Temperature Optimum: 40°C, Min. mold temperature: 30°C, Max. mold temperature: 40°C |