General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.14 g/cm³ Show Material materials with Densidad of 1.14 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Dureza Shore D | 23.0 °C | 45 [-] Show Material materials with Dureza Shore D of 45 [-] | max., ISO 7619-1 | ||
Elongación | 23.0 °C | 500 % Show Material materials with Elongación of 500 % | ISO 527-1/-2 | ||
Módulo elástico | 23.0 °C | 0.08 GPa Show Material materials with Módulo elástico of 0.08 GPa | ISO 527-1/-2 | ||
Resistencia a desgarros | 23.0 °C | 120 kN/m Show Material materials with Resistencia a desgarros of 120 kN/m | ISO 34-1 | ||
Resistencia a desgarros transversal | 23.0 °C | 120 kN/m Show Material materials with Resistencia a desgarros transversal of 120 kN/m | ISO 34-1 | ||
Resistencia a la tracción | 23.0 °C | 34 MPa Show Material materials with Resistencia a la tracción of 34 MPa | ISO 527-1/-2 | ||
Resistencia al choque, ensayo Charpy entallado | No Break @ -6,-40°C, ISO 179/1eA | ||||
Resistencia al choque, ensayo Izod no entallado | No Break @ -40°C,ISO 180/1A |
Aplicaciones térmicas
Property | Value | Comment | |
---|---|---|---|
Temperatura de fusión | 203 °C Show Material materials with Temperatura de fusión of 203 °C | ISO 11357-1/-3 | 18°F/min | |
Temperatura de reblandecimiento Vicat | 160 °C Show Material materials with Temperatura de reblandecimiento Vicat of 160 °C | ISO 306 | 90°F, 2 lbf | |
Inflamabilidad | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción transversal | 23.0 °C | 1.8 % Show Material materials with Contracción transversal of 1.8 % | ISO 294-4, 2577 |
Velocidad de flujo de la masa derretida | 6.5 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 6.5 g/10min | ISO 1133 | 230°C/10kg |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 110°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.08%, Melt Temperature Optimum: 240°C, Min. melt temperature: 230°C, Max. melt temperature: 250°C, Mold Temperature Optimum: 45°C, Min. mold temperature: 45°C, Max. mold temperature: 55°C |