General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 0.5 % Show Material materials with Absorción de agua of 0.5 % | Sim. to ISO 62 | Immersion 24h |
Densidad | 23.0 °C | 1.17 g/cm³ Show Material materials with Densidad of 1.17 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.49 [-] Show Material materials with Coeficiente de Poisson of 0.49 [-] | |||
Dureza Shore D | 23.0 °C | 55 [-] Show Material materials with Dureza Shore D of 55 [-] | max., ISO 7619-1 | ||
Elongación | 23.0 °C | 450 % Show Material materials with Elongación of 450 % | ISO 527-1/-2 | ||
Módulo de flexión | 23.0 °C | 0.16 GPa Show Material materials with Módulo de flexión of 0.16 GPa | ISO 178 | ||
Módulo elástico | 23.0 °C | 0.16 GPa Show Material materials with Módulo elástico of 0.16 GPa | ISO 527-1/-2 | ||
Resistencia a desgarros | 23.0 °C | 140 kN/m Show Material materials with Resistencia a desgarros of 140 kN/m | ISO 34-1 | ||
Resistencia a desgarros transversal | 23.0 °C | 100 kN/m Show Material materials with Resistencia a desgarros transversal of 100 kN/m | ISO 34-1 | ||
Resistencia a la tracción | 23.0 °C | 37 MPa Show Material materials with Resistencia a la tracción of 37 MPa | ISO 527-1/-2 | ||
Resistencia al choque, ensayo Charpy entallado | -40.0 °C | 30 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 30 kJ/m² | No Break @ 23°C, ISO 179/1eU | ||
-6.0 °C | 160 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 160 kJ/m² | No Break @ 23°C, ISO 179/1eU | |||
Resistencia al choque, ensayo Charpy no entallado | No Break @ 23°C, ISO 179/1eU |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Brittleness temperature | -100 °C Show Material materials with Brittleness temperature of -100 °C | ISO 974 | |||
Calor específico | 23.0 °C | 2100 J/(kg·K) Show Material materials with Calor específico of 2100 J/(kg·K) | of melt | ||
Coeficiente de dilatación térmica | 23.0 °C | 1.8E-4 1/K Show Material materials with Coeficiente de dilatación térmica of 1.8E-4 1/K | ISO 11359-1/-2 | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.8E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.8E-4 1/K | ISO 11359-1/-2 | ||
Difusividad térmica | 23.0 °C | 0 mm²/s Show Material materials with Difusividad térmica of 0 mm²/s | |||
Heat deflection temperature, 0.45 MPa | 57 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 57 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 41 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 41 °C | ISO 75-1/-2 | |||
Temperatura de fusión | 192 °C Show Material materials with Temperatura de fusión of 192 °C | ISO 11357-1/-3 | 18°F/min | |||
Temperatura de reblandecimiento Vicat | 170 °C Show Material materials with Temperatura de reblandecimiento Vicat of 170 °C | ISO 306 | 90°F, 2 lbf | |||
Temperatura de transición del vidrio | -30 °C Show Material materials with Temperatura de transición del vidrio of -30 °C | ISO 11357-1/-2 | 18°F/min | |||
Inflamabilidad | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, FMVSS Class: B -, Burning rate, Thickness 1 mm: 38 mm/min |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 1.7 % Show Material materials with Contracción of 1.7 % | ISO 294-4, 2577 |
Contracción transversal | 23.0 °C | 1.9 % Show Material materials with Contracción transversal of 1.9 % | ISO 294-4, 2577 |
Velocidad de flujo de la masa derretida | 6 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 6 g/10min | ISO 1133 | 230°C/10kg | |
Velocidad de flujo del volumen derretido | 6 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 6 cm³/10min | ISO 1133 |
Technological properties
Property | ||
---|---|---|
Fillers | Carbon Black | |
Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.08%, Melt Temperature Optimum: 240°C, Min. melt temperature: 230°C, Max. melt temperature: 250°C, Mold Temperature Optimum: 45°C, Min. mold temperature: 40°C, Max. mold temperature: 50°C |